CaCl~2-KCl熔体结构的X射线衍射分析

杨忠保;郭春泰;李洁;唐定骧   

  1. 中国科学院长春应用化学研究所
  • 出版日期:1992-03-15 发布日期:1992-03-15

Structure analysis of molten CaCl~2-KCl system by X-ray diffraction

YANG ZHONGBAO;GUO CHUNTIA;LI JIE;TANG DINGXIANG   

  • Online:1992-03-15 Published:1992-03-15

用高温液态X射线衍射方法, 测定了摩尔比为1:2的CaCl~2-KCl熔体的径向分布函数。结果表明, 熔体中Ca^2^+-Cl^-、K^+-Cl^-和Cl^--CL^-离子对间的最近邻距离分别为0.278,0.306和0.380nm。由于Ca^2^+与Cl^-间的强Coulomb作用, 在熔融的摩尔比为1:2的CaCl~2-KCl体系中, Cl^--Cl^-间的最近邻距离明显小于纯KCl熔体中Cl^--Cl^-间的最近邻距离。

关键词: X射线衍射分析, 结构分析, 结构与性能关系, 氯化钾, 熔盐, 氯化钙

Radial distribution function of CaCl2-KCl (1:2 mol) melt was measured by x-ray scattering of high temperature liquid The nearest neighbor distances of Ca2+-Cl-, K+-Cl- and Cl--Cl- ionic pairs are 0.278, 0.306 and 0.380 nm, resp. Relation is discussed between structure and physicochem. properties of the melt.