Block Copolymers Based on Polymethylene: Synthesis and Fabrication of Their Porous Films

Lü Huichao1,2 Xu Shengang1 Zhao Qiaoling2 Huang Jin2 Cao Shaokui*,1 Ma Zhi*,2   

  1. (1 School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450052)
    (2 Shanghai Institute of Organic Chemistry, Chinese Academy of Sciences, Shanghai 200032)
  • Received:2010-11-24 Revised:2010-12-24 Online:2011-05-14 Published:2011-01-04

Di- and tri-block copolymers based on polymethylene were synthesized via the combination of living polymerization of ylides and atomic transfer radical polymerization (ATRP). Firstly, hydroxyl terminated polymethylene (PM-OH) was synthesized via living polymerization of ylides followed by oxidation. The macroinitiator (PM-Br) was obtained by the reaction of PM-OH and 2-bromo-2-methylproplonyl bromide, then initiated the ATRP of tert-butyl acrylate to obtain PM-b-P-t-BA diblock copolymers. Subsequently, PM-b-P-t-BA-b-PS triblock copolymers were prepared using ATRP of styrene. Porous films of such di-block and tri-block copolymers were fabricated via breath-figure method with chloroform and carbon disulfide as solvent, respectively. The morphology of such porous film was observed by scanning electron microscopy (SEM). The effects of PS segment and temperature on the morphology of porous film were investigated.

Key words: polymethylene, block copolymer, breath figure, porous film