Wettability Analysis and Design of Micro-nanostructured Superhydrophobic Surface

doi:10.6023/A18100430

Acta Chim. Sinica ›› 2019, Vol. 77 ›› Issue (3): 269-277.DOI: 10.6023/A18100430 Previous Articles Next Articles

Article

微纳结构超疏水表面的浸润性分析及设计

马国佳^a, 郑海坤^b, 常士楠^b, 王硕硕^b

a 北京航空制造工程研究所高能束流加工技术国家重点实验室北京 100024;
b 北京航空航天大学航空科学与工程学院北京 100191

投稿日期:2018-10-16 发布日期:2018-12-03
通讯作者: 常士楠 E-mail:sn_chang@buaa.edu.cn
基金资助:
项目受国家自然科学基金（Nos.11672024，11372026）和国家重点基础研究发展计划项目（No.2015CB755803）资助.

Wettability Analysis and Design of Micro-nanostructured Superhydrophobic Surface

Ma Guojia^a, Zheng Haikun^b, Chang Shinan^b, Wang Shuoshuo^b

a Science and Technology on Power Beam Processes Laboratory, Beijing Aeronautical Manufacturing Technology Research Institute, Beijing 100024;
b School of Aeronautic Science and Engineering, Beihang University, Beijing 100191

Received:2018-10-16 Published:2018-12-03
Supported by:
Project supported by the National Natural Science Foundation of China (Grant Nos. 11672024, 11372026) and National Basic Research Program of China (Grants No. 2015CB755803).

1. Wettability Analysis and Design of Micro-nanostructured Superhydrophobic Surface.PDF(229KB)

Abstract

The special wettability of superhydrophobic surface usually has high contact angles (CA>150°) and low contact angle hysteresis (CAH<5°), which has been exploited for many potential applications. It is well known that wettability is mainly determined by micro/nano structure and surface composition, and various types of natural superhydrophobic surface could exhibit different wetting states, showing different wetting properties, such as low adhesive lotus leaf; the anisotropic superhydrophobic rice leaf; high adhesive rose petal. Therefore, the relationship between the wetting state and the surface structure should have a deeper understanding, especially in the design preliminary stage. The "droplet-superhydrophobic surface" system is taken as the research objects, four stable wetting state expressions are analyzed based on the principle of minimum energy. Wetting state transitions are studied on superhydrophobic surface coverd with micro/nano structured pillars of different distributions. The calculation formula of intrinsic contact angle is derived and the intrinsic contact angle of common materials is investigated. Based on the four wetting state of apparent contact angle equations, wetting diagrams were drew for investigating the wetting behavior, which include "one point, three lines, six areas, four state". The influence of the relative structure spacing and relative structure height on the wetting state is analyzed. It is found that the larger relative structure height, the smaller relative structure spacing, which can reduce the critical parameters of the transition state of the infiltration state, thereby expanding the range of the superhydrophobic surface, the more design options are available. It is also beneficial to the stability of the superhydrophobic surface, but should be controlled within certain scales because of mechanical stability. The simulation results accurately reflect the wetting state with the changes of the relative structure spacing and relative structure height. Finally, the general design of the superhydrophobic surface is refined. The results can provide theoretical guidance and technical fundament for the design of superhydrophobic surfaces.

Key words: wettability, superhydrophobic surface, critical relative structure spacing, critical relative structure height, design clue, wetting state transition

Cite this article

Ma Guojia, Zheng Haikun, Chang Shinan, Wang Shuoshuo. Wettability Analysis and Design of Micro-nanostructured Superhydrophobic Surface[J]. Acta Chim. Sinica, 2019, 77(3): 269-277.

Export EndNote|Reference Manager|ProCite|BibTeX|RefWorks

share this article

References

[1] Barthlott, W.; Neinhuis, C. Planta 1997, 202, 1.
[2] Marmur, A. Langmuir 2003, 19, 5956.
[3] Zheng, H. K.; Chang, S. N.; Zhao, Y. Y. Prog. Chem. 2017, 29, 102. (郑海坤, 常士楠, 赵媛媛, 化学进展, 2017, 29, 102.)
[4] Kreder, M. J.; Alvarenga, J.; Kim, P.; Aizenberg, J. Nat. Rev. Mater. 2016, 1, 15003.
[5] Liang, W. X.; Zhang, Y. B.; Wang, B.; Guo, Z. G.; Liu, W. M. Acta Chim. Sinica 2012, 70, 2393(梁伟欣, 张亚斌, 王奔, 郭志光, 刘维民, 化学学报, 2012, 70, 2393.)
[6] Zhang, J. N.; Yu, J. H. Chin. J. Chem. 2018, 36, 51.
[7] Cui, L. Y.; Fan, S. S.; Yu, C. L.; Kuang, M. X.; Wang, J. X. Acta Chim. Sinica 2017, 75, 967. (崔丽影, 范莎莎, 于存龙, 邝旻翾, 王京霞, 化学学报, 2017, 75, 967.)
[8] Wenzel, R. N. Ind. Eng. Chem. 1936, 28, 988.
[9] Cassie, A. B. D.; Baxter, S. Trans. Faraday Soc. 1944, 40, 546.
[10] Bico, J.; Tiele, U.; Quere, D. Colloid Surface A 2002, 206, 41.
[11] Bhushan, B.; Nosonovsky, M. Phil. Trans. R. Soc. A 2010, 368, 4713.
[12] Suzuki, S.; Ueno, K. Langmuir 2017, 33, 138.
[13] Hejazi, V.; Nosonovsky, M. Colloid Polym. Sci. 2013, 291, 329.
[14] Tuvshindorj, U.; Yildirim, A.; Ozturk, F. E.; Bayindir, M. ACS Appl. Mater. Inter. 2014, 6, 9680.
[15] Wang, S.; Jiang, L. Adv. Mater. 2007, 19, 3423.
[16] Rahmawan, Y.; Moon, M. W.; Kim, K. S. Langmuir 2009, 26, 484.
[17] Wu, B. B.; Wu, H. P.; Zhang, Z.; Dong, C. C.; Chai, G. Z. Acta Phys. Sin. 2015, 64, 176801. (吴兵兵, 吴化平, 张征, 董晨晨, 柴国钟, 物理学报, 2015, 64, 176801.)
[18] Lv, P. Y.; Xue, Y. H.; Duan, H. L. Adv. Mech. 2016, 46, 179. (吕鹏宇, 薛亚辉, 段慧玲, 力学进展, 2016, 46, 179.)
[19] Moosmann, M.; Schimmel, T.; Barthlott, W.; Mail, M. Beilstein J. Nanotech. 2017, 8, 1671.
[20] Seo, J.; García-Mayoral, R.; Mani, A. J. Fluid Mech. 2018, 8, 35.
[21] Lafuma, A.; Queré, D. Nat. Mater. 2003, 2, 457.
[22] Ye, X. M.; Zhang, X. S.; Li, M. L.; Li, C. X. Acta Phys. Sin. 2018, 67, 114702. (叶学民, 张湘珊, 李明兰, 李春曦, 物理学报, 2018, 67, 114702.)
[23] Kwon, H. M.; Paxson, A. T.; Varanasi, K. K.; Patankar, N. A. Phys. Rev. Lett. 2011, 106, 036102.
[24] Bartolo, D.; Bouamrirene, F.; Verneuil, É.; Buguin, A.; Silberzan, P.; Moulinet, S. EPL 2006, 74, 299.
[25] Bormashenko, E.; Pogreb, R.; Whyman, G.; Erlich, G. Langmuir 2007, 23, 12217.
[26] Girifalco, L. A.; Good, R. J. J. Phys. Chem. 1957, 61, 904.
[27] Zisman, W. A. Adv. Chem. 1964, 43, 1.
[28] Barthlott, W.; Neinhuis, C.; Cutler, D.; Ditsch, F.; Meusel, I.; Theisen, I. Bot. J. Linn. Soc. 1998, 126, 237.
[29] Nishino, T.; Meguro, M.; Nakamae, K. Langmuir 1999, 15, 4321.
[30] Han, J. T.; Sun, Y. K.; Woo, J. S.; Lee, G. W. Adv. Mater. 2010, 20, 3724.
[31] Raza, M. A.; Kooij, E. S.; Silfhout, A. Langmuir 2010, 26, 12962.
[32] Liu, X.; Dai, B.; Zhou, L.; Sun, J. J. Mater. Chem. 2009, 19, 497.
[33] Dong, J.; Jin, Y.; Dong, H.; Sun, L. Langmuir 2017, 33, 1041.
[34] Guan, Z. S.; Zhang, Q. Acta Chim. Sinica 2005, 63, 880. (管自生, 张强, 化学学报, 2005, 63, 880.)
[35] Kulinich, S. A.; Farhadi, S.; Nose, K. Langmuir 2011, 27, 25.

微纳结构超疏水表面的浸润性分析及设计

Wettability Analysis and Design of Micro-nanostructured Superhydrophobic Surface

PDF

Supporting Info.

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 9

Recommended Articles

Metrics

Comments

[1]	Lin Li, Zizhao Wang, Jiawei Liu, Jia Chen, Xiao Jin, Caili Dai. Synthesis and Performance Evaluation of Polyhydroxy Benzene Sulfonate Oil Displacement Agent Based on Enhanced Interfacial Wettability Control [J]. Acta Chimica Sinica, 2022, 80(1): 63-68.
[2]	Yining Ma, Run Shi, Tierui Zhang. Research Progress on Triphase Interface Electrocatalytic Carbon Dioxide Reduction [J]. Acta Chimica Sinica, 2021, 79(4): 369-377.
[3]	Sun Qi, Xiao Feng-Shou. Exploration of Porous Organic Polymers as a Platform for Biomimetic Catalysis [J]. Acta Chimica Sinica, 2020, 78(9): 827-832.
[4]	Cui Liying, Fan Shasha, Yu Cunlong, Kuang Minxuan, Wang Jingxia. Research Progress on the Super-wettability of Colloidal Photonic [J]. Acta Chim. Sinica, 2017, 75(10): 967-978.
[5]	Liang Weixin, Zhang Yabin, Wang Ben, Guo Zhiguang, Liu Weimin. Biological Applications of Biomimetic Superhydrophobic Surfaces [J]. Acta Chimica Sinica, 2012, 70(23): 2393-2403.
[6]	Wang Guojie Wang. The Study of Azobenzene Self-Assembled Monolayers Fabricated by Chemical Adsorption and Its Superhydrophobic Surface [J]. Acta Chimica Sinica, 2009, 67(13): 1417-1420.
[7]	TANG Yan-Jun^1,2; LI You-Ming*^,1; HU Da-Wei³. Modification, Surface Structure and Rheological Behavior of Nanosized CaCO₃ [J]. Acta Chimica Sinica, 2007, 65(20): 2291-2298.
[8]	GUAN Zi-Sheng*, ZHANG Qiang. Effect of Topography on Wettability of Pulse Laser-Ablated Si Surface [J]. Acta Chimica Sinica, 2005, 63(10): 880-884.
[9]	ZHANG FUTIAN. The wetting theory based on the interface layer model of physical interrace [J]. Acta Chimica Sinica, 1991, 49(7): 634-643.