三种不同碳链长度的双偶极半菁衍生物与WO3胶体粒子的静电自组装膜

邹旭1,2，范娅2，庄敏阳2，彭景2，高丽华*,1，王科志*,2   

  1. (1北京工商大学化学与环境工程学院 北京 100037)
    (2北京师范大学化学学院 北京 100875)
  • 投稿日期:2010-04-01 修回日期:2010-05-29 发布日期:2010-07-05
  • 通讯作者: 王科志 E-mail:kzwang@bnu.edu.cn
  • 基金资助:

    晶态薄膜材料及其全固态杂化太阳能电池的研究

Three Electrostatically Self-assembled Multilayer Films Prepared from Bipolar Hemicyanines and WO3 Colloidal Particles

Zou Xu1,2 Fan Ya2 Zhuang Minyang2 Peng Jing2, Gao Lihua*,1 Wang Kezhi*,2   

  1. (1 School of Chemical and Environmental Engineering, Beijing Technology and Business University, Beijing 100037)
    (2 College of Chemistry, Beijing Normal University, Beijing 100875)
  • Received:2010-04-01 Revised:2010-05-29 Published:2010-07-05
  • Contact: Ke-ZHi Wang E-mail:kzwang@bnu.edu.cn

PDF

1039

Three electrostatically self-assembled multilayer films were prepared by alternative adsorption of WO3 and three dipolar hemicyanine derivatives carrying one, three and six CH2, respectively and studied by UV-vis absorption spectroscopy and photoelectrochemistry. The films were uniformly deposited up to at least 12 layers, and have advantages of ready preparation, bathochromically shifted visible absorption bands and large photoelectric signals for the three CH2-containing hemicyanines, over previously reported Langmuir-Blodgett films of analogous hemicyanines.

Key words: hemicyanine, tungsten oxide, self-assembled film, UV-vis spectroscopy, photoelectric property