Optimal Synthesis and Sulfonylation Mechanism of a Novel Polyhedral Oligomeric Octadiphenylsulfonylsilsesquioxane

Li Ziqian, Yang Rongjie   

  1. School of Materials, Beijing Institute of Technology, Beijing 100081
  • Received:2014-05-13 Revised:2014-07-06 Published:2014-07-15
  • Supported by:

    Project supported by the National Natural Science Foundation of China (No.512730223).

PDF

1172

Octadiphenylsulfonylsilsesquioxane (ODPSS) was synthesized through sulfonylation of octaphenylsilsesquioxane (OPS) with benzenesulfonyl chloride and the AlCl3 catalyst in dichloromethane (CH2Cl2). By changing the solvent, catalyst, reaction time and molar ratio of reactants, the optimal reaction conditions were determined. It was found that OPS could be completely converted to ODPSS with a high yield. The product ODPSS was identified by FTIR, MALDI-TOF MS, 1H NMR, 13C NMR, 29Si NMR and elemental analysis. The reaction mechanism was analyzed and a sulfonylation model of OPS was established.

Key words: octadiphenylsulfonylsilsesquioxane, Friedel-Crafts sulfonylation, octaphenylsilsesquioxane