关键词: 离子热, 磷酸铝分子筛膜, 基底自转晶, 晶化机理

Highly c-oriented AEL aluminophosphate molecular sieve membranes were ionothermally synthesized on the surface of δ-alumina substrate by “Substrate Surface Conversion” method. The typical synthesis procedure can be described as follows: a δ-aluminia alumina disc was put into 1-ethyl-3-methyl imidazolium bromide ([EMIm]Br) solution containing reagent quantities of phosphoric acid (H₃PO₄) (85 wt% in water, AR) and hydrofluoric acid (HF) (40 wt% in water, AR). The synthesis was performed at 210 ℃ for certain time. No additional Al source is added into the synthesis solution. After the synthesis, the as-synthesized sample was washed thoroughly with distilled water and acetone for several times by ultrasonic vibration and dried at 120 ℃ overnight. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were carried out to characterize the products. The synthesis process of AEL membrane via “Substrate Surface Conversion” can be divided into two separated steps, which is carried out in the ionic liquid solution of HF and H₃PO₄ in turn. We termed this route as ionothermal two-step method, which making it possible for us to investigate the effect of HF and H₃PO₄, respectively. The formation mechanism of “Substrate Surface Conversion” was therefore demonstrated, with which the δ-alumina substrate acts as both support and Al source during the synthesis process. The surface of the substrate is first converted into a gel layer by the solution. The layer is a heterogeneous phase, which contains all nutrients required for the crystallization of molecular sieve membrane, including the aluminophosphate precursor, the mineralizer and the structure directing agent. The transformation from the gel layer into membrane is probably of solid-solid formation mechanism. The whole synthesis process needs the participation of both H₃PO₄ and HF. H₃PO₄ is an essential component of both aluminophosphate precursor and molecular sieve crystal. The crystallinity and the orientation of synthesized membranes can be greatly influenced by adjusting the amount of HF in the initial solution, which may act as both structure directing agent and mineralizer during the synthesis process of molecular sieve membrane.

Key words: ionothermal synthesis, aluminophosphate molecular sieve membrane, substrate surface conversion, formation mechanism