碳化多孔有机骨架制备氮掺杂多孔碳及其气体吸附研究

李艳强a, 贲腾b, 裘式纶a   

  1. a 吉林大学无机合成与制备化学国家重点实验室 长春 130012;
    b 吉林大学化学学院 长春 130012
  • 收稿日期:2015-01-31 出版日期:2015-06-14 发布日期:2015-04-23
  • 通讯作者: 贲腾, 裘式纶 E-mail:sqiu@jlu.edu.cn;tben@jlu.edu.cn
  • 基金资助:

    项目受国家自然科学基金(21390394, 21261130584, 21471065), 国家基础研究计划(2012CB821700),“111”计划(B07016), KAUST奖励项目(CRG-1-2012-LAI-009)和教育部科技发展中心项目(20120061130012)资助.

Preparation of N-doped Porous Carbon from Porous Organic Framework for Gas Sorption

Li Yanqianga, Ben Tengb, Qiu Shiluna   

  1. a State Key Laboratory of Inorganic Synthesis & Preparation Chemistry, Jilin University, Changchun 130012;
    b College of Chemistry, Jilin University, Changchun 130012
  • Received:2015-01-31 Online:2015-06-14 Published:2015-04-23
  • Supported by:

    Project supported by National Natural Science Foundation of China (Grant no. 21390394, 21261130584, 21471065), the National Basic Research Program of China (2012CB821700), the “111” project (B07016), the Award Project of KAUST (CRG-1-2012-LAI-009) and the Ministry of Education, Science and Technology Development Center Project (20120061130012).

In this report, a series of N-doped porous carbon materials were successfully prepared from nitrogen-containing porous organic framework JUC-Z2. Compared to original JUC-Z2, the carbonized samples show obviously enhanced gas uptake and isosteric heats of adsorption (Qst for short). Among the carbonized samples, JUC-Z2-900 shows high CO2 uptake of 113 cm3·g-1 at 273 K and 1 bar and H2 sorption of 246 cm3·g-1 at 77 K and 1 bar, surpassing most reported porous materials. Especially for CH4 sorption, a large sorption amount of 60 cm3·g-1 could be achieved at 273 K and 1 bar. To our best knowledge, this value is comparable to the highest among all the porous materials reported to date. Apart from high gas uptake, the carbon materials also show selective adsorption ability. At 273 K, JUC-Z2-900 shows a high CO2/N2 adsorption selectivity of 10 and CO2/H2 adsorption selectivity of 66. Raman spectra showed two Raman shifts, the G-band at 1590 cm-1 is associated with the E2g mode of graphite, whereas the D-band centered at around 1360 cm-1 is attributed to the D-band of disordered carbon, corresponding to the defect-induced mode. The intensity of D-band is higher than G-band, indicating a low degree of graphitization. This is also confirmed by powder X-ray diffraction results. X-ray Photoelectron Spectroscopy (XPS) results indicate the nitrogen content is 3.26 wt%, 2.88 wt% and 2.19 wt% for JUC-Z2-700, JUC-Z2-800 and JUC-Z2-900 respectively. Though the nitrogen content decreased after carbonization, the gas sorption increased greatly. This can be attributed to the increased heat of adsorption of the carbonized samples. First, the narrow pore size after carbonization is beneficial for gas storage. Reports indicate that by tuning the pore sizes to around the kinetic diameter of CO2, it may be possible to increase the number of double or multiple interactions between the adsorbed CO2 and the pore walls. Second, the all-carbon-scaffold networks also benefit the gas-adsorbent interaction. Last but not the least, the N-doped framework also devote the high gas uptake. Besides the high gas uptake, the carbon materials exhibit high thermal stabilities and could be stable up to 500 ℃. Based on the above results, the carbon materials show great potential in the fields of CO2 capture and clean energy storage.

Key words: porous organic frameworks, porous carbons, CO2 sorption, H2 storage, selective adsorption