Solvothermal Preparation and Characterization of Nano-nickel Oxide

doi:10.6023/A19010033

Acta Chim. Sinica ›› 2019, Vol. 77 ›› Issue (5): 447-454.DOI: 10.6023/A19010033 Previous Articles Next Articles

Article

溶剂热法制备纳米氧化镍及其表征

陈甜, 杨英, 赵婉玉, 潘德群, 朱从潭, 林飞宇, 郭学益

中南大学冶金与环境学院长沙 410083

投稿日期:2019-01-19 发布日期:2019-04-22
通讯作者: 杨英, 郭学益 E-mail:muyicaoyang@126.com;xyguo@csu.edu.cn
基金资助:
项目受国家自然科学基金（61774169）、留学回国基金、湖南省自然科学基金（2016JJ3140）和中南大学本科生创新项目（ZY20180866，202321009）资助.

Solvothermal Preparation and Characterization of Nano-nickel Oxide

Chen Tian, Yang Ying, Zhao Wanyu, Pan Dequn, Zhu Congtan, Lin Feiyu, Guo Xueyi

Central South University, School of Metallurgy and Environment, Changsha 410083

Received:2019-01-19 Published:2019-04-22
Contact: 10.6023/A19010033 E-mail:muyicaoyang@126.com;xyguo@csu.edu.cn
Supported by:
Project supported by the National Natural Science Foundation of China (No. 61774169), Scientific Research Foundation for the Returned overseas Chinese Scholar, Natural Science Foundation of Hunan Province (2016JJ3140) and Undergraduate student of Central South University (ZY20180866,202321009).

Nano-scale nickel oxide materials were prepared by solvothermal method using nickel acetylacetonate, oleic acid and oleylamine as raw materials, octadecene as solvent and polyvinylpyrrolidone as surfactant. The effects of the ratio of reactants ratio, insulation time, surfactant and the mass of oleylamine on the microstructure, particle size, morphology, optics and catalytic properties of the product were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM), ultraviolet-visible spectroscopy (UV-Vis) spectral analysis, and Tafel test. The specific experimental operations were:the oleic acid (OA) and 1-octadecene (ODE) was added into four flasks (500 mL) with heating and stirring. Nickel acetylacetonate was added when the temperature raise to 50℃, then continuously stirring for 60 minutes at 120℃ before a certain amount of oleylamine (OAm) was added to the reaction system. The mixed solution was poured into the inner liner of the high temperature reactor. The reactor was covered and transferred to the electro-thermostatic blast oven for a period of time and then cooled to room temperature. The main research results were obtained:(1) The boundary of the original particles became smoothed after sintering, and the spherical particles become flake-shaped which might be attributed to the residual organic covering so the size of nickel oxide nanoparticles changed from the original 40~45 nm to 30~40 nm. (2) With the addition of PVP, the content of NiO phase increased and the particle size was controlled within 40~45 nm. The UV-Vis test showed that NiO belonged to direct band gap and the band gap width was 3.5~3.7 eV. (3) The Tafel analysis showed that the best catalytic activity with exchange current density J₀ was 1.23×10^-2 mA·cm^-2, where pure NiO could be obtained when the reactant ratio of n[Ni(acac)₂]:n(OA)=1:2, the additive PVP mass fraction was of 1.66%, the amount of oleylamine was of 30 mmol, and the temperature was of 200℃ for 8 h.

Key words: NiO nanoparticles, solvothermal method, ratio of reactants, surfactant, microstructure and optical properties

Cite this article

Chen Tian, Yang Ying, Zhao Wanyu, Pan Dequn, Zhu Congtan, Lin Feiyu, Guo Xueyi. Solvothermal Preparation and Characterization of Nano-nickel Oxide[J]. Acta Chim. Sinica, 2019, 77(5): 447-454.

Export EndNote|Reference Manager|ProCite|BibTeX|RefWorks

share this article

References

[1] Lin, X.-Y.; Wang, J. Acta Chim. Sinica 2017, 75, 979(in Chinese). (林潇羽, 王璟, 化学学报, 2017, 75, 979.)
[2] Gu, T.-H.; Shi, J.-M.; Hua, Y.-L.; Liu, J.; Wang, W.; Zhang, W.-X. Acta Chim. Sinica 2017, 75, 991(in Chinese). (顾天航, 石君明, 滑熠龙, 刘静, 王伟, 张伟贤, 化学学报, 2017, 75, 991.)
[3] Guo, X.-R.; Yin, Y.-G.; Tan, Z.-Q.; Liu, J.-F.; Jiang, G.-B. Acta Chim. Sinica 2018, 76, 387(in Chinese). (郭肖茹, 阴永光, 谭志强, 刘景富, 江桂斌, 化学学报, 2018, 76, 387.)
[4] Zhang, W.; Deng, W. Chin. J. Org. Chem. 2018, 38, 3002(in Chinese). (张薇, 邓维, 有机化学, 2018, 38, 3002.)
[5] Wang, L.; Zhao, D.-D.; Liu, X.; Yu, P.; Fu, H.-G. Acta Chim. Sinica 2017, 75, 231(in Chinese). (王蕾, 赵冬冬, 刘旭, 于鹏, 付宏刚, 化学学报, 2017, 75, 231.)
[6] Martin, C. R. Science 1994, 266, 1961.
[7] Zhao, J.; Chen, Z. J. Comput. Theor. Nanosci. 2011, 8, 2395.
[8] Liu, L.; Li, Y.; Yuan, S.; Ge, M.; Ren, M.; Sun, C.; Zhou, Z. J. Phys. Chem. C 2010, 114, 1.
[9] Huang, X.; Tan, C.-L.; Yin, Z.-Y.; Zhang, H. Adv. Mater. 2014, 26, 14.
[10] Sawatzky, G. A.; Allen, J. W. Phys. Rev. Lett. 1984, 53, 24.
[11] Thota, S.; Shim, J. H.; Seehra, M. S. J. Appl. Phys. 2013, 114, 21.
[12] Das, N.-S.; Santra, S.; Banerjee, D.; Das, G.-C.; Chattopadhyay, K. K. Mater. Res. Express. 2014, 1, 2.
[13] Echresh, A.; Chan, O.-C.; Shoushtari, M.-Z.; Khranovskyy, V.; Nur, O.; Willander, M. J. Alloys Compd. 2015, 632, 25.
[14] Hashemzadeh, F.; Gaffarinejad, A.; Rahimi, R. J. Hazard. Mater. 2015, 286, 9.
[15] Wang, G.; Yang, D.-M.; Liu, J. Mater. Rev. 2017, 31, 5(in Chinese). (王刚, 杨定明, 刘江, 材料导报, 2017, 31, 5.)
[16] Jang, Y.; Chen, D.-D.; Song, J.-S.; Jiao, Z.; Ma, Q.-L.; Zhang, H.-J.; Cheng, L.-L.; Zhao, B.; Chu, Y.-L. Electrochim. Acta 2013, 91, 3.
[17] Yan, X.-Y.; Tong, X.-L.; Wang, J.; Gong, C.-W.; Zhang, M.-G.; Liang, L.-P. Mater. Lett. 2013, 95, 3.
[18] Wang, H.; Zeng, X.-W.; Huang, Z.-F.; Zhang, W.-J.; Qiao, X.-F.; Hu, B.; Zou, X.-P.; Wang, M.-K.; Cheng, Y.-B.; Chen, W. ACS Appl. Mater. Interfaces 2014, 6, 15.
[19] Song, C.; Dong, X.-T.; Wang, J.-X.; Liu, G.-X. Acta Chim. Sinica 2011, 69, 20(in Chinese). (宋超, 董相廷, 王进贤, 刘桂霞, 化学学报, 2011, 69, 20.)
[20] Jia, W.; Xu, M.-W.; Lei, C.; Bao, S.-J.; Jia, D.-Z. Acta Chim. Sinica 2011, 69, 15(in Chinese). (贾巍, 徐茂文, 雷超, 包淑娟, 贾殿赠, 化学学报, 2011, 69, 15.)
[21] Zhang, H.-J.; Zhang, X.-G.; Yuan, C.-Z.; Gao, B.; Sun, K.; Fu, Q.-B.; Lu, X.-J.; Jiang, J.-C. Acta Phys.-Chim. Sin. 2011, 27, 2(in Chinese). (张海军, 张校刚, 原长洲, 高博, 孙康, 傅清宾, 卢向军, 蒋剑春, 物理化学学报, 2011, 27, 2.)
[22] Jiang, L.; Huang, H.; Wang, C.-T.; Zhang, W.-K.; Gan, Y.-P.; Tao, X.-Y. Acta Phys.-Chim. Sin. 2016, 26, 02(in Chinese). (蒋磊, 黄辉, 王春涛, 张文魁, 甘永平, 陶新永, 物理化学学报, 2016, 26, 02.)
[23] Ma, X.-J.; Wang, N.-N.; Qian, Y.-T.; Bai, Z.-C. Mater. Lett. 2016, 168, 5.
[24] Miao, R.-Y.; Zeng, W. Mater. Lett. 2016, 171, 200.
[25] Turgut, G.; Duman, S. J. Alloys Compd. 2016, 664, 547.
[26] Zhao, J.-F.; Tan, Y.; Su, K.; Zhao, J.-J.; Yang, C.; Sang, L.-L.; Lu, H.-B.; Chen, J.-H. Appl. Surf. Sci. 2015, 337, 111.
[27] Patil, R.-A.; Devan, R.-S.; Lin, J.-H.; Ma, Y.-R.; Patil, P.-S.; Liou, Y. Sol. Energy Mater. Sol. Cells 2013, 112, 91.
[28] Jiang, H.; Jian, J.-W.; Chen, K.; Gu, Y.-Y. J. Chin. Ceram. Soc. 2012, 40, 12.
[29] Ma, X.-J.; Wang, N.-N.; Qian, Y.-T.; Bai, Z.-C. Mater. Lett. 2016, 168, 5.
[30] Cai, G.-F.; Wang, X.; Cui, M.-Q.; Darmawan, P.; Wang, J.-X.; Eh, A. L.-S.; Lee, P.-S. Nano Energy 2015, 12, 258.
[31] Yang, P.-P.; Yuan, X.-L.; Hu, H.-C.; Liu, Y.-L.; Zheng, H.-W.; Yang, D.; Chen, L.; Cao, M.-H.; Yong, X.; Min, Y.-L.; Li, Y.-G.; Zhang, Q. Adv. Funct. Mater. 2018, 28, 1.
[32] Zhang, Q.; Zheng, Z.; Liu, C.-X.; Liu, C.-Q.; Tan, T.-W. Colloids Surf., B 2016, 140, 446.
[33] Liu, J.; Sun, Z.-K.; Deng, Y.-H.; Zou, Y.; Li, C.-Y.; Guo, X.-H.; Xiong, L.-Q.; Gao, Y.; Li, F.-U.; Zhao, D.-Y. Angew. Chem., Int. Ed. 2009, 48, 32.
[34] Mali, S.-S.; Kim, H.; Kim, H.-H.; Shim, S.-E.; Hong, C.-K. Mater. Today 2018, 21, 483.
[35] Liu, Z.-H.; Z, A.-L.; C, F.-S.; Tao, L.-M.; Zhou, Y.-H.; Zhao, Z.-X.; Chen, Q.; Cheng, Y.-B.; Zhou, H.-P. J. Mater. Chem. A 2017, 5, 6597.
[36] (a) Jeng, J.-Y.; Chen, K.-C.; Chiang, T.-Y.; Lin, P.-Y.; Tsai, T.-D.; Chang, Y.-C.; Guo, T.-F.; Chen, P.; Wen, T.-C.; Hsu, Y.-J. Adv. Mater. 2014, 26, 4107.
(b) Tian, H.-N.; Xu, B.; Chen, H.; Johansson, E. M. J.; Boschloo, G. ChemSusChem 2014, 7, 8.
[37] Irwin, M.-D.; Buchholz, B.; Hains, A.-W.; Chang, R. P. H.; Marks, T.-J. Proc. Natl. Acad. Sci. 2008, 105, 8.
[38] Zhu, Z.-L.; Bai, Y.; Zhang, T.; Liu, Z.-K.; Long, X.; Wei, Z.-H.; Wang, Z.-L.; Zhang, L.-X.; Wang, J.-N.; Yan, F.; Yang, S.-H. Angew. Chem. 2014, 26, 46.
[39] Guo, X.-Y.; Wang, W.-J.; Yang, Y.; Tian, Q.-H. CrystEngComm 2016, 10, 1039.
[40] Su, D.; Ford, M.; Wang, G.-X. Sci. Rep. 2012, 2, 924.
[41] Ahn, Y.; Jang, J.; Son, J.-Y. J. Electroceram. 2017, 38, 1.
[42] Fan, J.-L.; Wang, S.-Z.; Sun, W.; Guo, S.-G.; Kang, Y.; Du, J.-J.; Peng, X.-J. CrystEngComm 2016, 64, 3.
[43] Saha, S.; Chhetri, S.; Khanra, P.; Samanta, P.; Koo, H.; Murmu, N.-C.; Kuila, T. J. Energ. Storage 2016, 6, 22.
[44] Abu-Zied, B.-M.; Asiri, A.-M. Thermochim. Acta 2017, 649, 54.
[45] Gao, J.; Yang, Y.; Zhang, Z.; Yan, J.-Y.; Lin, Z.-H.; Guo, X.-Y. Nano Energy 2016, 26, 123.
[46] Li, Y.-J.; Quan, F.-X.; Chen, L.; Zhang, W.-J.; Yu, H.-B.; Chen, C.-F. RSC Adv. 2013, 4, 1895.
[47] Liu, Z.-H.; Zhang, M.; Xu, X.-B.; Bu, L.-L.; Zhang, W.-J.; Li, W.-H.; Zhao, Z.-X.; Wang, M.-K.; Cheng, Y.-B.; He, H.-S. Dalton Trans. 2015, 44, 3967.
[48] Gao, W.; Xia, Z.-M.; Cao, F.-X.; Ho, J.-C.; Jiang, Z.; Qu, Y.-Q. Adv. Funct. Mater. 2018, 28, 1706056.

溶剂热法制备纳米氧化镍及其表征

Solvothermal Preparation and Characterization of Nano-nickel Oxide

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Chenyu Liao, Shanwei Guo, Meiwei Huang, Yong Guo, Qing-Yun Chen, Chao Liu, Yunwen Zhang. Synthesis and Properties of Fluoroether Phosphocholine [J]. Acta Chimica Sinica, 2024, 82(1): 46-52.
[2]	Lin Li, Zizhao Wang, Jiawei Liu, Jia Chen, Xiao Jin, Caili Dai. Synthesis and Performance Evaluation of Polyhydroxy Benzene Sulfonate Oil Displacement Agent Based on Enhanced Interfacial Wettability Control [J]. Acta Chimica Sinica, 2022, 80(1): 63-68.
[3]	Zhao Weiwei, Wang Yilin. Development of Surfactant Application in Wastewater Treatment [J]. Acta Chim. Sinica, 2019, 77(8): 717-728.
[4]	Li Haofei, Qiao Fulin, Fan Yaxun, Wang Yilin. Aggregation in the Mixture of Branched Carboxylate Salts and Sulfonate Surfactants with Different Oligomeric Degrees [J]. Acta Chim. Sinica, 2018, 76(7): 564-574.
[5]	Yan Nana, Xiao Tianliang, Liu Zhaoyue. Monolayer-gated Ion Transport in Artificial Ion Channels Based on A Nanoporous Gold Membrane [J]. Acta Chim. Sinica, 2017, 75(9): 873-877.
[6]	Zhang Na, Chen Guojun, Chen Kun, Li Hongguang, Hao Jingcheng. Viscoelastic Emulsions Stabilized by Salt-Free Catanionic Surfactants [J]. Acta Chim. Sinica, 2015, 73(8): 835-839.
[7]	Sha Min, Zhang Ding, Pan Renming, Xing Ping, Jiang Biao. Synthesis and Properties Study of Novel Branched Fluorinated Surfactants with CF₃CF₂CF₂C(CF₃)₂ Group [J]. Acta Chim. Sinica, 2015, 73(5): 395-402.
[8]	Tang Yongqiang, Zhu Linyi, Han Yuchun, Wang Yilin. Effects of Branched-Chain Alcohols on Surface Activity and Micellization of Gemini Surfactants [J]. Acta Chimica Sinica, 2014, 72(6): 673-681.
[9]	Wang Ruijuan, Wang Yilin. Interaction of Anionic Sulfonate Gemini Surfactant with PEO-PPO-PEO Triblock Copolymers [J]. Acta Chimica Sinica, 2014, 72(1): 41-50.
[10]	Guo Hong, Wang Dong, Dong Shuli, Dou Yingying, Song Aixin, Hao Jingcheng. Self-assembly and Rheological Properties of C₁₂EO₄ and Aminosilane Mixtures [J]. Acta Chimica Sinica, 2013, 71(08): 1129-1135.
[11]	Huang Xu, Han Yuchun, Wang Yilin. Thermodynamic Investigation on Micellization of Cationic Gemini Surfactants with Nitrophenoxy Groups in Hydrophobic Chains [J]. Acta Chimica Sinica, 2013, 71(06): 897-905.
[12]	Su Ke, Jiang Hongbin, Zhu Deming, Fu Haiyan, Zheng Xueli, Yuan Maolin, Li Ruixiang, Chen Hua . Study on 1-Octene Hydroformylation Promoted by Cetyltrihydroxyethyl Ammonium Bromide in Aqueous/Organic Biphasic Solution [J]. Acta Chimica Sinica, 2013, 71(05): 844-848.
[13]	Chen Dongdong, Wang Lin, Sun Junqi. High Efficient Loading of Hydrophobic Molecules in Layer-by-Layer Assembled Microgel Films with the Assistance of Surfactant Micelles [J]. Acta Chimica Sinica, 2012, 70(17): 1779-1784.
[14]	Chu Zonglin, Zhang Yongmin, Han Yugui, Wang Hongyan, Li Bin, Feng Yujun. Shear Banding Transition of Wormlike Micelles Formed by a C₂₂-Tailed Cationic Surfactant [J]. Acta Chimica Sinica, 2012, 70(14): 1551-1554.
[15]	Liu Guoyu, Gu Daming, Liu Haiyan, Ding Wei, Yu Tao, Cheng Jiecheng. Molecular Dynamics Simulation of Ionic Liquid-type Gemini Imidazolium Surfactants in Aqueous Solutions [J]. Acta Chimica Sinica, 2012, 70(01): 6-14.