含能配位聚合物[Pb(tza)2]n的合成、结构与性能研究

李志敏1, 张国涛1,2, 张同来*,1, 张建国1, 杨利1, 周遵宁1 齐书元1, 郁开北1, 赵凤起3, 仪建华3, 徐司雨3, 高洪旭3   

  1. (1北京理工大学爆炸科学与技术国家重点实验室 北京 100081)
    (2中国航天科技集团公司四院四十二所 襄樊 441003)
    (3西安近代化学研究所 西安 710065)
  • 投稿日期:2010-07-08 修回日期:2010-08-18 发布日期:2011-01-18
  • 通讯作者: 张同来 E-mail:ztlbit@bit.edu.cn
  • 基金资助:

    国家自然科学基金;爆炸科学与技术国家重点实验室基金

Synthesis, Structural Investigation and Properties of A Novel Energetic Coordination Polymer [Pb(tza)2]n

Li Zhimin1,Zhang Guotao1,2,Zhang Tonglai*,1,Zhang Jianguo1,Yang Li1,Zhou Zunning1,Qi Shuyuan1,Yu Kaibei1,Zhao Fengqi3,Yi Jianhua3,Xu Siyu3,Gao Hongxu3   

  1. (1 State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing 100081)
    (2 The 42nd Institute of the Fourth Academy of China Aerospace Science and Technology Corporation, Xiangfan 441003)
    (3 Xi an Modern Chemistry Research Institute, Xi an 710065)
  • Received:2010-07-08 Revised:2010-08-18 Published:2011-01-18
  • Contact: Tong-lai Zhang E-mail:ztlbit@bit.edu.cn

PDF

1322

四氮唑乙酸与碳酸铅反应制备得到含能配位聚合物[Pb(tza)2]n (Htza＝四氮唑-1H-1-乙酸), 用自然蒸发母液法获得单晶. 运用元素分析和红外光谱对结构进行了表征, X射线单晶衍射结果表明: 该晶体属于单斜晶系, C2/c空间群, a＝1.5370(5) nm, b＝1.0373(3) nm, c＝0.8261(3) nm, β＝119.415(4)°, V＝1.1473(7) nm3, ρ＝2.671 g/cm3, Z＝2. 采用差示扫描量热分析(DSC)和热重-微分热重分析(TG-DTG)研究了该配合物的热分解过程及其非等温反应动力学, 并根据相关标准对配合物进行了感度测试. 结果表明: 该含能配合物具有较好的热稳定性和适当的感度, 分解反应放出大量的热和气体产物, 有望作为含能材料应用于相关领域.

关键词: 含能配位聚合物, 四氮唑乙酸, 晶体结构, 热分析

A novel energetic coordination polymer [Pb(tza)2]n was synthesized by the reaction of PbCO3 and tetrazole-1-acetic acid in water solution, and characterized by elemental analysis and Fourier transform infrared (FT-IR) spectra. The crystal structure was investigated by using single-crystal X-ray diffraction, and it belongs to monoclinic system with space group C2/c, a＝1.5370(5) nm, b＝1.0373(3) nm, c＝0.8261(3) nm, β＝119.415(4)°, V＝1.1473(7) nm3, ρ＝2.671 g/cm3, Z＝2. The thermal decomposition process of [Pb(tza)2]n and non-isothermal kinetics analysis were investigated by using DSC and TG-DTG methods, also its sensitivities were tested according to the specifications. The study results verify that [Pb(tza)2]n presents good properties for potential application as an energetic material.

Key words: energetic coordination polymer, tetrazole-1-acetic acid, crystal structure, thermal property