化学学报 ›› 2019, Vol. 77 ›› Issue (1): 90-94.DOI: 10.6023/A18080318 上一篇    下一篇

研究论文

Pd催化层对含氧氢化钇(YHx:O)薄膜光致变色调节能力的影响

拉毛a,b, 包山虎a,b, 莎仁a   

  1. a 内蒙古师范大学化学与环境科学学院 呼和浩特 010020;
    b 中国科学院上海硅酸盐研究所工业陶瓷研究中心 上海 200050
  • 投稿日期:2018-08-05 发布日期:2018-09-30
  • 通讯作者: 莎仁 E-mail:994042048@qq.com
  • 基金资助:

    项目受国家自然科学基金(No.51272271)资助.

Effect of the Pd Layer on Optical Regulation Properties of the Oxygen Containing Yttrium Hydrides

La Maoa,b, Bao Shan-Hua,b, Sha Rena   

  1. a Department of Chemistry and Environmental Science, Inner Mongolia Normal University, Hohhot 010020;
    b State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050
  • Received:2018-08-05 Published:2018-09-30
  • Contact: 10.6023/A18080318 E-mail:994042048@qq.com
  • Supported by:

    Project supported by the National Natural Science Foundation of China (No. 51272271).

含氧氢化钇(YHx:O)薄膜是一种新型的光致变色材料,因其特殊的光学特性在光致变色调光镜领域有着广泛的应用前景.然而,该薄膜光致变色原理尚处于探索阶段,且光致变色性能、变色速率以及循环耐久性等特性有待改善.本研究中,采用直流磁控溅射法在YHx:O薄膜表面镀了一层具有催化氢功能的金属Pd层,探索其对薄膜光学调节率、晶体结构、表面微观形貌以及各个元素含量变化的影响.通过对薄膜进行一系列表征得知,Pd层可以促进YHx:O薄膜光致着色过程,提高薄膜可见及太阳光光学调节能力10%左右.从薄膜EDS数据中可以看到,光照后双层薄膜内部氧含量减少,而金属钇相对增多,该结果与单层薄膜一致.

关键词: YHx:O, 氢化钇, 光致变色, 节能材料

Photochromic materials of oxygen-containing yttrium hydride exhibit reversible switching properties that can find applications in the energy saving windows, optical switching devices. However, the photochromic mechanisms of the oxygen-containing yttrium hydride has been not clarified yet. The optical modulation and durability of the films need to be improved. In this paper, oxygen-containing yttrium hydride films covered with hydrogen catalytic-palladium layers were prepared on a glass substrate by a direct-current (DC) magnetron sputtering methods. Firstly, oxygen-containing yttrium hydride thin films were deposited by DC magnetron sputtering of the Y targets in a 0.4 Pa with argon (purity 6N) and hydrogen (5N) mixed gas. Secondly, a thin film of Pd was deposited on the surface of YHx:O layer. Moreover, the effects of the Pd layer in the optical regulation state, crystal structure, surface microstructure and the content of each element of the oxygen-containing yttrium hydride films were investigated by means of SEM, XRD, and XPS methods. In the initial state, the films showed a transparent state with high transmittance in the visible and near-IR range same with single layer of the YHx:O. After exposure to xenon or visible light, the solar transmittance (Tsol) of the films sharply decreased by 37.39%. The result can be found that the coloring process (illumination process) of YHx:O thin films can be promoted and the optical regulation range can be increased after covered with a Pd layer. Investigation of the crystal structure by XRD demonstrates YHx:O covered with Pd, the same crystalline state with the YHx:O thin films has been found. After illumination, all reflection peaks of the YHx:O films slightly moving towards the larger angles with smaller lattice parameter (~5.30 Å) due to the deoxidation of YHx:O films. It can be seen from the EDS data that the oxygen contents in the YHx:O film decreases, while the yttrium contents increases, which is consistent with that of the single layer films. The XPS survey scans analysis of the YHx:O and Pd/YHx:O was also studied. After illumination, all peaks of the single layer slightly moving towards the larger angles. But the double layer have reverse result with above.

Key words: YHx:O, yttrium hydride, photochromic, energy saving materials