Li10GeP2S12固态电解质电极界面特性研究

doi:10.6023/A19010013

摘要/Abstract

采用高温固相法合成了固态电解质Li₁₀GeP₂S₁₂，其室温离子电导率为2.02×10^-3 S/cm，并组装了LiNbO₃@LiNi_1/3Co_1/3Mn_1/3O₂/Li₁₀GeP₂S₁₂/Li全固态电池.恒流充放电测试表明全固态电池首次放电容量121.2 mAh/g，库伦效率40周后稳定在99.8%左右，循环100周后容量保持率达93.7%.电化学阻抗谱的测试结果表明，其典型的阻抗谱图由高频区半圆（HFS）、中频区半圆（MFS）和低频区斜线（LFL）组成，其中，HFS归属于电解质阻抗（R_el//Q_el），MFS归属于电荷传递过程（R_ct//Q_dl），LFL归属于锂离子的固态扩散过程.通过选取适当的等效电路，对实验所得的电化学阻抗谱数据进行拟合，并分析了R_el和R_ct随电极电位的变化规律.

关键词: 全固态电池, Li₁₀GeP₂S₁₂, 电化学阻抗谱, 电荷传递电阻

All-solid-state batteries will be the main direction of lithium-ion batteries in the future. Current research mainly focuses on improving the conductivity of solid-state electrolytes, but there are few studies on the electronic and ionic transport in all solid state batteries. In this paper, we synthesized Li₁₀GeP₂S₁₂ through high temperature solid phase method. The ionic conductivity of Li₁₀GeP₂S₁₂ at room temperature is 2.02×10^-3 S/cm and it's activation energy calculated from Arrhenius plots is 29.8 kJ/mol. The all solid-state battery of LiNbO₃@LiNi_1/3Co_1/3Mn_1/3O₂/Li₁₀GeP₂S₁₂/Li was successfully fabricated and characterized by galvanostatic charge/discharge (DC), cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The first discharge capacity of the all-solid-state battery is 121.2 mAh/g, the coulombic efficiency stabilize at 99.8% after 40 weeks and the capacity retention rate is 93.7% after 100 weeks. After analyzing the electrochemical impedance spectroscopy, the typical impedance spectra of the battery is composed of high frequency semicircle (HFS), middle frequency semicircle (MFS) and low frequency line (LFL). And HFS belongs to the impedance of electrolyte (R_el), MFS belongs to charge transfer impedance (R_ct) and LFL belongs to diffusion process of lithium ion in active material. The continuous increase of R_el between 3.8 V and 4.3 V is due to the decomposition of LGPS to GeS₂, S and P₂S₅ at high potential, which results in the decrease of grain conductivity. On the other hand, the voltage range of 3.8~4.3 V is near the charging and discharging plateau at which concentration polarization is large. The stress in the crystal may lead to the breakup of some grains which resulting in the generation of more grain boundaries and the increase of grain boundary impedance. According to the fitting results of R_ct, we find that R_ct decreases with the increase of potential until 4.3 V at which R_ct reaches the minimum value in the first process of charging and it is a reversible process while discharging.

Key words: all solid state batteries, Li₁₀GeP₂S₁₂, electrochemical impedance spectroscopy, charge transfer resistance

引用此文

张桐, 杨梓, 李红亮, 庄全超, 崔艳华. Li₁₀GeP₂S₁₂固态电解质电极界面特性研究[J]. 化学学报, 2019, 77(6): 525-532.

Zhang Tong, Yang Zi, Li Hongliang, Zhuang Quanchao, Cui Yanhua. Electrochemical Impedance Spectroscopic Studies of All Solid State battery with Li₁₀GeP₂S₁₂ as Electrolyte[J]. Acta Chim. Sinica, 2019, 77(6): 525-532.

导出引用 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

分享此文

参考文献

[1] Goodenough, J. B.; Kim, Y. Chem. Mater. 2010, 22, 587.
[2] Jin, Z. Q.; Xie, K.; Hong, X. B. Acta Chim. Sinica 2014, 72, 11(in Chinese). (金朝庆, 谢凯, 洪晓斌, 化学学报, 2014, 72, 11.)
[3] Liu, J.; Xu, J. Y.; Lin, Y.; Li, J.; Lai, Y. Q.; Yuan, C. F.; Zhang, J.; Zhu, K. Acta Chim. Sinica 2013, 71, 869(in Chinese). (刘晋, 徐俊毅, 林月, 李劼, 赖延清, 袁长福, 张锦, 朱凯, 化学学报, 2013, 71, 869.)
[4] Bachman, J. C.; Muy, S.; Grimaud, A.; Chang, H. H.; Pour, N.; Lux, S. F.; Paschos, O.; Maglia, F.; Lupart, S.; Lamp, P. Chem. Rev. 2016, 47, 140.
[5] Lin, D.; Liu, Y.; Cui, Y. Nat. Nanotechnol. 2017, 12, 194.
[6] Qiu, Z.; Zhang, Y.; Xia, S.; Dong, P. Acta Chim. Sinica 2015, 73, 992(in Chinese). (邱振平, 张英杰, 夏书标, 董鹏, 化学学报, 2015, 73, 992.)
[7] Liu, W. Y.; Fu, Z. W.; Qin, Q. Z. Acta Chim. Sinica 2004, 62, 2223(in Chinese). (刘文元, 傅正文, 秦启宗, 化学学报, 2004, 62, 2223.)
[8] Deng, Z.; Mo, Y.; Ong, S. P. NPG Asia Mater. 2016, 8, e254.
[9] Manthiram, A.; Yu, X.; Wang, S. Nat. Rev. Mater. 2017, 2, 16103.
[10] Ramakumar, S.; Deviannapoorani, C.; Dhivya, L.; Shankar, L. S.; Murugan, R. Prog. Mater. Sci. 2017, 88, 325.
[11] Xu, H. H.; Wang, S. F.; Wilson, H.; Zhao, F.; Manthiram, A. Chem. Mater. 2017, 29, 7206.
[12] Zhang, B.; Rui, T.; Yang, L.; Zheng, J.; Zhang, K.; Mo, S.; Zhan, L.; Feng, P. Energy Storage Mater. 2018, 10, 139.
[13] He, X.; Zhu, Y.; Mo, Y. Nat. Commun. 2017, 8, 15893.
[14] Fergus, J. W. J. Power Sources 2010, 195, 4554.
[15] Minami, T.; Hayashi, A.; Tatsumisago, M. Solid State Ion. 2006, 177, 2715.
[16] Luo, W.; Gong, Y.; Zhu, Y.; Li, Y.; Yao, Y.; Zhang, Y.; Fu, K. K.; Pastel, G.; Lin, C. F.; Mo, Y. Adv. Mater. 2017, 29, 1606042.
[17] Zhu, Y.; He, X.; Mo, Y. J. Mater. Chem. A 2016, 4, 3253.
[18] Wang, Q.; Wen, Z.; Jin, J.; Guo, J.; Huang, X.; Yang, J.; Chen, C. Chem. Commun (Camb). 2016, 52, 1637.
[19] Li, Y.; Zhou, W.; Chen, X.; Lü, X.; Cui, Z.; Xin, S.; Xue, L.; Jia, Q.; Goodenough, J. B. Proc. Natl. Acad. Sci. U. S. A. 2016, 113, 13313.
[20] Kato, A.; Hayashi, A.; Tatsumisago, M. J. Power Sources 2016, 309, 27.
[21] Zhu, Y.; He, X.; Mo, Y. ACS Appl. Mater. Interfaces 2015, 7, 23685.
[22] Sharafi, A.; Kazyak, E.; Davis, A. L.; Yu, S.; Thompson, T.; Siegel, D. J.; Dasgupta, N. P.; Sakamoto, J. Chem. Mater. 2017, 29, 7961.
[23] Takada, K. Langmuir 2013, 29, 7538.
[24] Yokokawa, H. Solid State Ion. 2016, 285, 126.
[25] Long, P.; Xu, Q.; Peng, G.; Yao, X.; Xu, X. ChemElectroChem 2016, 3, 764.
[26] Wan, H.; Gang, P.; Yao, X.; Jing, Y.; Ping, C.; Xu, X. Energy Storage Mater. 2016, 4, 59.
[27] Nagao, M.; Kitaura, H.; Hayashi, A.; Tatsumisago, M. J. Power Sources 2009, 189, 672.
[28] Gao, J.; Zhao, Y. S.; Shi, S. Q.; Li, H. Chinese Phys. B 2016, 25, 35.
[29] Haruyama, J.; Sodeyama, K.; Tateyama, Y. ACS Appl. Mater. Interfaces 2017, 9, 286.
[30] Tatsumisago, M.; Nagao, M.; Hayashi, A. J. Asian Ceram. Soc. 2013, 1, 17.
[31] Noriaki, K.; Kenji, H.; Yuichiro, Y.; Masaaki, H.; Ryoji, K.; Masao, Y.; Takashi, K.; Yuki, K.; Shigenori, H.; Koji, K. Nat. Mater. 2011, 10, 682.
[32] Amani, J. A.; Koppe, T.; Hofsäss, H.; Vetter, U. Phys. Rev. Appl. 2015, 4, 044007.
[33] Zhuang, Q. C.; Xu, S. D.; Qiu, X. Y.; Cui, Y. L.; Fang, L.; Sun, S. G. Prog. Chem. 2010, 22, 1044(in Chinese). (庄全超, 徐守冬, 邱祥云, 崔永丽, 方亮, 孙世刚, 化学进展, 2010, 22, 1044.)
[34] Siroma, Z.; Sato, T.; Takeuchi, T.; Nagai, R.; Ota, A.; Ioroi, T. J. Power Sources 2016, 316, 215.
[35] Boulineau, S.; Courty, M.; Tarascon, J. M.; Viallet, V. Solid State Ion. 2012, 221, 1.
[36] Han, F.; Gao, T.; Zhu, Y.; Gaskell, K. J.; Wang, C. Adv. Mater. 2015, 27, 3473.
[37] Qiu, X. Y.; Zhuan, Q. C.; Zhang, Q. Q.; Cao, R.; Qiang, Y. H.; Ying, P. Z.; Sun, S. G. J. Electroanal. Chem. 2013, 688, 392.
[38] Liu, W.; Sun, D.; Feng, T.; Xia, J.; Wang, Q.; Jiang, D. J. Ceram. 2013, 34, 555(in Chinese). (刘薇, 孙大志, 冯涛, 夏金峰, 王琪, 蒋丹宇, 陶瓷学报, 2013, 34, 555.)
[39] Verkerk, M.; Middelhuis, B.; Burggraaf, A. Solid State Ion. 1982, 6, 159.
[40] Näfe, H. Solid State Ion. 1984, 13, 255.
[41] Mo, Y.; Ong, S. P.; Ceder, G. Chem. Mater. 2012, 24, 15.
[42] Levi, M. D.; Gamolsky, K.; Aurbach, D.; Heider, U.; Oesten, R. Electrochim. Acta 2000, 45, 1781.
[43] Ohta, N.; Takada, K.; Sakaguchi, I.; Zhang, L. Q.; Ma, R. Z.; Fukuda, K.; Osada, M.; Sasaki, T. Electrochem. Commun. 2007, 9, 1486.

Li₁₀GeP₂S₁₂固态电解质电极界面特性研究

Electrochemical Impedance Spectroscopic Studies of All Solid State battery with Li₁₀GeP₂S₁₂ as Electrolyte

PDF

可视化

摘要/Abstract

引用此文

分享此文

参考文献

相关文章 15

编辑推荐

相关统计

本文评价

[1]	张冠华, 杨子涵, 马越. 混合工艺对氧化物/硫化物复合固态电解质电化学性能的影响[J]. 化学学报, 2023, 81(10): 1387-1393.
[2]	梁世硕, 康树森, 杨东, 胡建华. 锂金属负极界面修饰及其在硫化物全固态电池中的应用[J]. 化学学报, 2022, 80(9): 1264-1268.
[3]	吕泽伟, 韩敏芳, 孙再洪, 孙凯华. 固体氧化物燃料电池运行初期电化学性能演变机制[J]. 化学学报, 2021, 79(6): 763-770.
[4]	唐笑, 汪禹汛. 染料敏化太阳能电池中低染料吸附浓度下的界面电荷复合效应[J]. 化学学报, 2013, 71(02): 193-198.
[5]	张胜寒, 梁可心, 檀玉. 电化学阻抗谱法研究铈改性TiO₂ 纳米管阵列光电极裂解水产氢动力学[J]. 化学学报, 2012, 70(9): 1109-1116.
[6]	龙萍, 李庆芬, 许立坤, 薛丽莉, 宋泓清. 钌镧氧化物涂层在NaCl 溶液中的电化学阻抗谱(EIS)研究[J]. 化学学报, 2012, 70(10): 1166-1172.
[7]	陈智栋, 陈转霞, 汤佳丽, 许娟, 王文昌, 曹剑瑜. 高分散的介孔碳载Pt 纳米粒子的制备及其对乙二醇的电催化氧化性能[J]. 化学学报, 2012, 70(03): 241-246.
[8]	吴超, 庄全超, 徐守冬, 崔永丽, 强颖怀, 孙智. α-Fe₂O₃/C复合材料的制备及性能研究[J]. 化学学报, 2012, 70(01): 51-57.
[9]	杜莉莉, 庄全超, 魏涛, 史月丽, 强颖怀, 孙世刚. Si/C复合材料电极首次嵌锂过程的电化学阻抗谱研究[J]. 化学学报, 2011, 69(22): 2641-2647.
[10]	邓萌, 汪茫, 陈红征. 聚吡咯涂层的电化学合成及对神经微电极电性能的影响[J]. 化学学报, 2011, 69(04): 477-482.
[11]	魏涛, 庄全超, 吴超, 崔永丽, 方亮, 孙世刚. 温度对尖晶石LiMn₂O₄中锂离子嵌脱过程的影响[J]. 化学学报, 2010, 68(15): 1481-1486.
[12]	李松梅, 张媛媛, 杜娟, 刘建华, 于美. A3钢在氧化亚铁硫杆菌、链霉菌及其混合菌体系中的腐蚀行为[J]. 化学学报, 2010, 68(01): 67-74.
[13]	庄全超, 魏涛, 魏国祯, 董全峰, 孙世刚. 尖晶石LiMn2O4中锂离子嵌入脱出过程的电化学阻抗谱研究[J]. 化学学报, 2009, 67(19): 2184-2192.
[14]	王艳珍,钟庆东,巫欣欣,施利毅. ZnO-Bi2O3二元陶瓷粉体电化学行为研究[J]. 化学学报, 2009, 67(15): 1743-1748.
[15]	樊小勇,庄全超,魏国祯,柯福生,黄令,董全峰,孙世刚. 电化学阻抗谱法研究Cu₆Sn₅合金负极相变过程[J]. 化学学报, 2009, 67(14): 1547-1552.