芴酮对聚醚侧链聚芴体系的影响: 合成, 表征及光物理性质的研究

张冰1，浦侃裔1，范曲立2，裴启兵3，汪联辉*,1，黄维*,2   

  1. (1复旦大学先进材料实验室 上海 200433)
    (2南京邮电大学先进材料研究院 南京 210003)
    (3 Department of Material Science and Engineering, University of California at Los Angeles, L.A., CA 90095, USA)
  • 投稿日期:2007-03-25 修回日期:2007-09-26 发布日期:2008-05-28
  • 通讯作者: 汪联辉

Effect of Fluorenone on the Polyfluorenes with Polar Tri(ethylene oxide) Side Chains and Their Synthesis, Characterization and Photophysics

ZHANG, Bing1, PU, Kan-Yi1, FAN, Qu-Li2, PEI, Qi-Bing3, WANG, Lian-Hui*,1, HUANG, Wei*,2   

  1. (1 Laboratory of Advanced Materials, Fudan University, Shanghai 200433, China)
    (2 Institute of Advanced Materials, Nanjing University of Posts and Telecommunications, Nanjing 210003, China)
    (3 Department of Material Science and Engineering, University of California at Los Angeles, L.A., CA 90095, USA)
  • Received:2007-03-25 Revised:2007-09-26 Published:2008-05-28
  • Contact: Wang Lian-Hui

PDF

842

Cited

2

A series of fluorene-fluorenone copolymers constituted by 9,9-di(3,6,9-trioxadecyl)-fluorene and 9-fluorenone moieties in different molar ratios have been synthesized by Yamamoto coupling reactions. By means of the UV-Vis and PL emission spectra of solution and solid state film, the effect of fluorenone acting as an energy acceptor on the energy transfer process and the photophysics of the copolymers was investigated. In dilute solution, the fluorescence of the polyfluorene backbone was dominant and the energy transfer depended on the polymer concentration strongly. The energy transfer efficiency of the thin film was enhanced rapidly with increasing the fluorenone content and the phenomenon became more distinct after being annealed.

Key words: polyfluorene, fluorenone, energy transfer, photophysics