Acta Chimica Sinica ›› 2011, Vol. 69 ›› Issue (01): 53-58. Previous Articles     Next Articles

Full Papers

以诺卡氏菌为模板的微纳米Ni-Fe-P吸波材料的制备及性能研究

韩宇,李松梅*,刘建华,于美   

  1. (北京航空航天大学材料科学与工程学院 空天材料与服役教育部重点实验室 北京 100191)
  • 投稿日期:2010-03-23 修回日期:2010-08-06 发布日期:2010-08-30
  • 通讯作者: 李松梅 E-mail:buaa_lee@sina.com
  • 基金资助:

    航空科学基金资助项目

Preparation and Performance of Wave Absorbing Materials by Metallization of Nocadia

HAN Yu, LI Song-Mei, LIU Jian-Hua, YU Mei   

  1. (Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering, Beihang University, Beijing 100191)
  • Received:2010-03-23 Revised:2010-08-06 Published:2010-08-30

Micro/nano Ni-Fe-P wave absorbing materials were prepared on the surface of Nocadia pretreated by electroless plating technique. The morphology, component, structure and magnetic property were characterized by SEM, EDS, XRD and VSM. The results clearly demonstrated that one-step method was in a condition to deposit on the surface of Nocadia, and the surface of plating was roughed with the increase of the spherical particles and decomposition products due to the effects of the load, the quality of plating and the utilization of electroless solution were the best when the load was 80 mL. The average contents of Ni, Fe and P element of the metal layer with 80 mL load (w) were about 83.17%, 6.12% and 10.71%, respectively. The magnetic property was changed little by increasing of the load, and the plating was amorphous. The electromagnetic parameters were measured by VNA, the results showed that the reflection loss could reach 27 dB at the frequency of 10~12 and 15~17 GHz when the thickness was 2 mm.

Key words: electroless, nocadia, pretreatment, load, wave absorbing materials