Acta Chimica Sinica ›› 2007, Vol. 65 ›› Issue (9): 793-797. Previous Articles Next Articles
Original Articles
韩长秀*, 林徐明, 张宝贵
投稿日期:
修回日期:
发布日期:
通讯作者:
HAN Chang-Xiu*; LIN Xu-Ming; ZHANG Bao-Gui
Received:
Revised:
Published:
Contact:
Share
Co-P amorphous alloy and a new supported Co-P amorphous alloy catalyst CoP/TiO2 were prepared respectively by reduction-chemical deposition method. The physical properties of the alloy catalysts were characterized by XRD, ICP, TEM, BET and DSC. The structure, composition, shape, surface area and thermal stabilities of Co-P and CoP/TiO2 were compared. Besides, their catalytic activities for PH3 decomposition were compared, too. Compared with Co-P particles, CoP/TiO2 has bigger surface area, higher thermal stability and catalytic activity, which was attributed to interaction of TiO2 support and catalyst and high dispersion of Co-P alloy particles on the support of TiO2.
Key words: amorphous alloy, Co-P alloy, titania, supported catalyst
HAN Chang-Xiu*; LIN Xu-Ming; ZHANG Bao-Gui. Effect of Support TiO2 on the Characteristics of Co-P Amorphous Alloy[J]. Acta Chimica Sinica, 2007, 65(9): 793-797.
Export EndNote|Reference Manager|ProCite|BibTeX|RefWorks