水热合成介观结构的ZnS纳米纤维

化学学报 ›› 2004, Vol. 62 ›› Issue (22): 2273-2276. 上一篇下一篇

研究论文

水热合成介观结构的ZnS纳米纤维

李军平^1,2, 翟尚儒^1,2, 刘勇^1,2, 徐耀¹, 吴东¹, 孙予罕¹

1. 中国科学院山西煤炭化学研究所, 煤转化国家重点实验室, 太原, 030001;
2. 中国科学院研究生院, 北京, 100039

投稿日期:2004-03-11 修回日期:2004-07-25 发布日期:2014-02-17
通讯作者: 孙予罕,E-mail:yhsun@sxicc.ac.cn E-mail:yhsun@sxicc.ac.cn

Hydrothermal Synthesis of Mesostructured ZnS Nanofibers

LI Jun-Ping^1,2, ZHAI Shang-Ru^1,2, LIU Yong^1,2, XU Yao¹, WU Dong¹, SUN Yu-Han¹

1. State Key Laboratory of Coal Conversion, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001;
2. Graduate School of Chinese Academy of Sciences, Beijing 100039

Received:2004-03-11 Revised:2004-07-25 Published:2014-02-17

文章分享

摘要/Abstract

以Zn(Ac)₂和Na₂S为原料、EDTA为稳定剂、OA为结构导向模板,采用水热合成方法成功地制备了具有层状介观结构的ZnS纳米纤维;通过XRD, TEM, SEM, N₂-吸附/脱附以及紫外-可见漫反射等手段对所得的产物进了表征,并初步探讨了其形成机理.

关键词: ZnS, 纳米纤维, 介观结构, 形貌

Novel lamellar mesostructured ZnS nanofibers with uniform diameter in about 20～40 nm and length up to several micrometers have been facilely synthesized via hydrothermal reaction of Zn(Ac)₂ and Na₂S using neutral octylamine (OA) as structure-directing agent and ethylene diamine tetraacetic acid (EDTA) as stabilizer. The as-synthesized products were characterized via XRD, TEM, SEM, N₂ adsorption isotherms and the UV-visible absorption spectra. A possible formation mechanism for the mesostructured nanofibers was also discussed.

Key words: ZnS, nanofiber, mesostructure, morphology

引用此文

李军平, 翟尚儒, 刘勇, 徐耀, 吴东, 孙予罕. 水热合成介观结构的ZnS纳米纤维[J]. 化学学报, 2004, 62(22): 2273-2276.

LI Jun-Ping, ZHAI Shang-Ru, LIU Yong, XU Yao, WU Dong, SUN Yu-Han. Hydrothermal Synthesis of Mesostructured ZnS Nanofibers[J]. Acta Chimica Sinica, 2004, 62(22): 2273-2276.

导出引用 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

分享此文

参考文献

[1] Yu, C.-Z.; Fan, J.; Zhao, D.-Y. Acta Chim. Sinica 2002, 60, 1357 (in Chinese).(余承忠, 范杰, 赵东元, 化学学报, 2002, 60, 1357.)
[2] Zhai, S.-R.; Zhang, Y.; Wu, D.; Sun, Y.-H. Acta Chim. Sinica 2003, 61, 345 (in Chinese).(翟尚儒, 张晔, 吴东, 孙予罕, 化学学报, 2003, 61, 345.)
[3] Kim, S.; Zhang, W.; Pinnavaia, T. J. Science 1998, 282, 1302.
[4] Zhang, D.; Feng, J.; Huo, Q.; Melosh, N.; Fredrickson, G. H.; Chmelka, B. F.; Stucky, G. D. Science 1998, 279, 548.
[5] Zhang, Z.; Han, Y.; Xiao, F.; Qiu, S.; Zhu, M.; Wang, R.; Yu, Y.; Zhang, Z.; Zou, B.; Wang, Y.; Sun, H.; Zhao, D.; Wei, Y. J. Am. Chem. Soc. 2001, 123, 5014.
[6] Xu, A.-W.; Yu, J.-C.; Cai, Y.-P.; Zhang, H.-X.; Zhang, L.-Z. Chem. Commun. 2002, 1614.
[7] Lin, W.; Pang, W.; Sun, J.; Shen, J. J. Mater. Chem. 1999, 9, 641.
[8] Mal, N. K.; Ichikawa, S.; Fujiwara, M. Chem. Commun. 2002, 112.
[9] Sokolov, I.; Jiang, T.; Ozin, G. A. Adv. Mater. 1998, 10, 942.
[10] Chen, S.; Liu, W.-M. Chem. J. Chin. Univ. 2000, 21, 472 (in Chinese).(陈爽, 刘维民, 高等学校化学学报, 2000, 21, 472.)
[11] Zhu, Y.; Bando, Y.; Uemura, Y. Chem. Commun. 2003, 836.
[12] (a) Jiang, X. C.; Xie, Y.; Lu, J.; Zhu, L. Y.; He, W.; Qian, Y. T. Chem. Mater. 2001, 13, 1213.
(b) Wu, Q.; Zheng, N.; Ding, Y.; Li, Y. Inorg. Chem. Commun. 2002, 671.
[13] Ma, Y.; Qi, L.; Ma, J.; Cheng, H. Langmuir 2003, 19, 4040.
[14] Yu, S. H.; Yoshimura, M. Adv. Mater. 2002, 14, 296.
[15] Li, J.; Kessler, H.; Soulard, M.; Khouchaf, L.; Tuilier, M. H. Adv. Mater. 1998, 10, 946.
[16] (a) Huo, Q.; Margolese, D. I.; Ciesla, U.; Demuth, D. G.; Feng, P.; Gier, T. E.; Sieger, P.; Firouzi, A.; Chmelka, B. F.; Schuth, F.; Stucky, G. D. Chem. Mater. 1994, 6, 1176.
(b) Gabashvili, A.; Seisenbaeva, G. A.; Kessler, V. G.; Zhang, L. Z.; Yu, J. C.; Gedanken, A. J. Mater. Chem. 2003, 13, 2851.

水热合成介观结构的ZnS纳米纤维

Hydrothermal Synthesis of Mesostructured ZnS Nanofibers

PDF

可视化

被引次数

摘要/Abstract

引用此文

分享此文

参考文献

相关文章 15

编辑推荐

相关统计

本文评价

[1]	刘佳, 陈光海, 陈轶群, 江杰涛, 肖霄, 吴强, 杨立军, 王喜章, 胡征. 碳热还原活化扩孔提升介观结构碳纳米笼超级电容器性能^★[J]. 化学学报, 2023, 81(7): 709-716.
[2]	牛犇, 翟振宇, 郝肖柯, 任婷莉, 李从举. 基于ZIF-8/PAN复合薄膜的柔性丙酮气体传感器[J]. 化学学报, 2022, 80(7): 946-955.
[3]	刘彦甫, 李世麟, 荆亚楠, 肖林格, 周惠琼. 有机太阳能电池性能衰减机理研究进展[J]. 化学学报, 2022, 80(7): 993-1009.
[4]	Jamshid Kadirkhanov, 钟峰, 张文建, 洪春雁. 聚合诱导自组装制备多腔室囊泡以及成核链段中亲溶剂片段的影响[J]. 化学学报, 2022, 80(7): 913-920.
[5]	王志琴, 项博, 黄晓宇, 陆国林, 冯纯. 磷钨酸对对苯撑乙烯撑寡聚物-b-聚(2-乙烯基吡啶)自晶种行为的影响^※[J]. 化学学报, 2022, 80(3): 297-302.
[6]	郝肖柯, 翟振宇, 孙亚昕, 李从举. 柔性可水洗的Zr-MOFs复合纳米纤维薄膜的制备和性能表征[J]. 化学学报, 2022, 80(1): 49-55.
[7]	苗俊辉, 丁自成, 刘俊, 王利祥. 小分子给体/高分子受体型有机太阳能电池研究进展[J]. 化学学报, 2021, 79(5): 545-556.
[8]	李乐乐, 向阳阳, 刘欢, 麻拴红, 李斌, 马正峰, 魏强兵, 于波, 周峰. 亚表面引发原子转移自由基聚合构筑温度响应型纳米纤维油水分离膜[J]. 化学学报, 2021, 79(3): 353-360.
[9]	李宸, 陈凤华, 叶丽, 李伟, 于晗, 赵彤. B,N共掺杂的In₂O₃/TiO₂制备与光催化产氢性能研究[J]. 化学学报, 2020, 78(12): 1448-1454.
[10]	张宇, 王世兴, 杨蕊, 戴腾远, 张楠, 席聘贤, 严纯华. Co₉S₈/MoS₂异质结构的构筑及电催化析氢性能研究[J]. 化学学报, 2020, 78(12): 1455-1460.
[11]	陈甜, 杨英, 赵婉玉, 潘德群, 朱从潭, 林飞宇, 郭学益. 溶剂热法制备纳米氧化镍及其表征[J]. 化学学报, 2019, 77(5): 447-454.
[12]	杨靖鸽, 李阳, 王小艾, 王栋, 孙亚伟, 王继乾, 徐海. 环二肽的自组装及其荧光性能[J]. 化学学报, 2019, 77(12): 1279-1286.
[13]	王玲, 杨国锐, 王嘉楠, 王思岚, 彭生杰, 延卫. 静电纺丝在钠离子电池中的应用研究进展[J]. 化学学报, 2018, 76(9): 666-680.
[14]	黄璐, 李志春, 黄寿强, Peter Reiss, 李良. 持续注射法合成InPZnS/ZnS核壳结构量子点的研究[J]. 化学学报, 2017, 75(3): 300-306.
[15]	马慧, 马巍, 杨哲曜, 丁志峰, 龙亿涛. 纳米电极稳态电流表征的探讨[J]. 化学学报, 2017, 75(11): 1082-1086.