Preparation of Polypyrrole-Carbon Black Supported Pd Catalyst for Formic Acid Electrooxidation

Liu Jiajia^a, Wu Bing^a,b, Gao Ying^a,b

a College of Chemistry and Chemical Engineering, Harbin Normal University, Harbin 150025;
b Key Laboratory of Design and Synthesis of Functional Materials and Green Catalysis, Harbin 150025

Received:2012-01-09 Published:2012-06-14
Supported by:
Project supported by the Natural Science Foundation of Heilongjiang Province (Nos. B200905, B201002), the Youth Fund of Harbin Science and Technology Bureau (No. 2010RFXXG018) and Program for Scientific and Technological Innovation Team Construction in Universities of Heilongjiang (No. 2011TD010).

文章分享

摘要/Abstract

通过低温氧化法在活性碳表面修饰聚吡咯(PPy-C), 并以PPy-C为载体制备了纳米Pd催化剂(Pd/PPy-C). 采用X射线衍射、扫描电镜、透射电镜等手段对载体PPy-C及催化剂Pd/PPy-C进行了表征, 电化学测试结果表明, Pd/PPy-C催化剂电极不但能够增强催化剂对甲酸催化氧化的活性, 而且还能够大幅度提高催化剂的稳定性, 因此以PPy-C为载体的Pd/PPy-C催化剂是一类具有潜在应用前景的直接甲酸燃料电池阳极催化剂. 通过分析电化学比表面随循环伏安次数的变化及多电势阶跃实验结果表明, 催化剂电极活性衰减的主要原因是载体被氧化及电极表面积累强吸附物种的结果.

关键词: Pd, 聚吡咯, 甲酸, 电催化剂

Direct formic acid fuel cells are environmentally friendly technologies and have attracted more and more attention as a new generation of power source. Pd is an important noble metal that is widely used in heterogeneous catalysis. In order to disperse Pd nanoparticles and to improve their catalytic efficiency and stability, polypyrrole are generally used as supporting materials due to their structures and electrical properties. In this work, polypyrrole composite (PPy-C) encompassed of carbon black are synthesized by low temperature oxidation of pyrrole on carbon black and the nanosized Pd catalyst supported by PPy-C is prepared. The support PPy-C and the catalyst Pd/PPy-C are characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The TEM results show that the morphology of Pd/PPy-C and Pd/PPy-C is not the same. Pd deposited on PPy-C are nanoparticle clusters. The average particle size of metal Pd in Pd/C and Pd/PPy-C catalysts are 4.2 and 3.8 nm obtained from XRD diffraction peak. The results from formic acid oxidation show that the Pd/PPy-C catalyst exhibits better activity and stability in contrary to Pd/C. After 160 potential cycles, the formic acid oxidation current reduced to 8% of the first lap on Pd/C, but 50% on Pd/PPy-C. Therefore, the Pd/PPy-C catalyst is a promising anode catalyst in direct formic acid fuel cells. By analyzing formic acid oxidation current in the experiment of multi-step potential, it shows that the main reasons of the decrease of the oxidation current are the unstabitily of the support and the strong adsorption species on the electrode surface.

Key words: Pd, polypyrrole, formic acid, electrocatalyst

引用此文

刘佳佳, 邬冰, 高颖. 聚吡咯-碳载Pd催化剂的制备及对甲酸的电催化氧化[J]. 化学学报, 2012, 70(16): 1743-1747.

Liu Jiajia, Wu Bing, Gao Ying. Preparation of Polypyrrole-Carbon Black Supported Pd Catalyst for Formic Acid Electrooxidation[J]. Acta Chimica Sinica, 2012, 70(16): 1743-1747.

导出引用 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

分享此文

参考文献

[1] Uhm, S.; Lee, H. J.; Lee, J. PCCP 2009, 11, 9326.

[2] Ma, Y. J.; Yang, M. X.; Wang, W. F.; Zhou, M.; Liu, J.; Li, T. T.; Chen, H. Acta Chim. Sinica 2011, 69, 262. (马永钧, 杨梅霞, 王伟峰, 周敏, 刘婧, 李婷婷, 陈慧, 化学学报, 2011, 69, 262.)
[3] Serov, A.; Kwak, C. Appl. Catal. B: Environ. 2009, 91, 1.

[4] Antolini, E. Energy Environ. Sci. 2009, 2, 915.

[5] Liu, Y.; Wang, L. W.; Wang, G.; Deng, C.; Wu, B.; Gao, Y. J. Phys. Chem. C 2010, 114, 21417.
[6] Pan, Y. H.; Zhang, R. M.; Blair, S. L. Electrochem. Solid-State Lett. 2009, 12, B23.

[7] Zhang, S. X.; Qing, M.; Zhang, H.; Tian, Y. N. Electrochem. Commun. 2009, 11, 2249.

[8] Zhang, L.; Li, F. Electrochim. Acta 2010, 55, 6695.

[9] Zhao, Y. C.; Wang, F. Y.; Tian, J. N.; Yang, X. L.; Zhan, L. Electrochim. Acta 2010, 55, 8998.

[10] Sun, Z. P.; Zhang, X. G.; Tong, H.; Liang, Y. Y.; Li, H. L. J. Colloid Interface Sci. 2009, 337, 614.

[11] Ji, X. L.; Lee, K. T.; Holden, R.; Zhang, L.; Zhang, J. J.; Botton, G. A.; Couillard, M.; Nazar, L. F. Nat. Chem. 2010, 2, 286.

[12] Tu, D. D.; Wu, B.; Wang, B. X.; Deng, C.; Gao, Y. Appl. Catal. B: Environ. 2011, 103, 163.

[13] Liu, Z. L.; Zhang, X. H.; Hong, L. Electrochem. Commun. 2009, 11, 925.

[14] Dhaoui, W.; Hasik, M.; Djurado, D.; Bernasik, A.; Pron, A. Synth. Met. 2010, 160, 2546.

[15] Liao, C.; Wei, Z. D.; Chen, S. G.; Li, L.; Ji, M. B.; Tan, Y.; Liao, M. J. J. Phys. Chem. C 2009, 113, 5705.

[16] Wang, Z.; Zhu, Z. Z.; Li, H. L. Acta Chim. Sinica 2007, 65, 1149. (王喆, 朱赞赞, 力虎林, 化学学报, 2007, 65, 1149.)
[17] Selvaraj, V.; Alagar, M.; Kumar, K. S. Appl. Catal. B: Environ. 2007, 75, 129.

[18] Ding, K. Q.; Jia, H. T.; Wei, S. Y.; Guo, Z. H. Ind. Eng. Chem. Res. 2011, 50, 7077.

[19] Qu, B.; Xu, Y. T.; Lin, S. J.; Zheng, Y. F.; Dai, L. Z. Synth. Met. 2010, 160, 732.

[20] Yang, S.; Shen, C.; Liang, Y.; Tong, H.; He, W.; Shi, X.; Zhang, X.; Gao, H.-J. Nanoscale 2011, 3, 3277.

[21] Ding, K.; Jia, H.; Wei, S.; Guo, Z. Ind. Eng. Chem. Res. 2011, 50, 7077.

[22] Radmilovic, V.; Gasteiger, H. A.; Ross, P. N. J. Catal. 1995, 154, 98.

[23] Zhou, Y.; Liu, J. G.; Ye, J. L.; Zou, Z. G.; Ye, J. H.; Gu, J.; Yu, T.; Yang, A. D. Electrochim. Acta 2010, 55, 5024. Yu, X. W.; Pickup, P. G. Electrochem. Commun. 2009, 11, 2012.

聚吡咯-碳载Pd催化剂的制备及对甲酸的电催化氧化

Preparation of Polypyrrole-Carbon Black Supported Pd Catalyst for Formic Acid Electrooxidation

PDF

可视化

被引次数

摘要/Abstract

引用此文

分享此文

参考文献

相关文章 15

编辑推荐

相关统计

本文评价

[1]	徐续盼, 范凯, 赵胜泽, 李健, 高珊, 吴忠标, 孟祥举, 肖丰收. 介孔Beta沸石负载钯在甲烷催化燃烧反应中的性能研究^★[J]. 化学学报, 2023, 81(9): 1108-1112.
[2]	刘春梅, 高燕均, 陈鹏亮. 直接甲酸钠/铁氰化钾微流体燃料电池性能研究[J]. 化学学报, 2022, 80(9): 1256-1263.
[3]	谢晨帆, 徐玉平, 高明亮, 徐忠宁, 江海龙. MOF基Pd单位点催化CO酯化制碳酸二甲酯[J]. 化学学报, 2022, 80(7): 867-873.
[4]	蒋银龙, 李国超, 陈青松, 徐忠宁, 林姗姗, 郭国聪. 富晶格位错的多孔铋纳米花高效电还原二氧化碳制甲酸盐^※[J]. 化学学报, 2022, 80(6): 703-707.
[5]	应霞薇, 浮建军, 曾敏, 刘文, 张天宇, 沈培康, 张信义. 基于BiOCl-Fe₂O₃@TiO₂介孔复合材料的光电化学合成氨性能研究[J]. 化学学报, 2022, 80(4): 503-509.
[6]	陈莹莹, 刘欢, 程彦, 谢青季. 动态氢气泡/牺牲铜模板法制备蜂窝AuPt_Cu电催化剂用于甲酸氧化[J]. 化学学报, 2020, 78(4): 330-336.
[7]	宋波, 秦安军, 唐本忠. 绿色单体二氧化碳参与的新型聚合反应[J]. 化学学报, 2020, 78(1): 9-22.
[8]	傅方舟, 张志诚, 孙倩怡, 徐冰, 沙菁㛃. 纳米孔技术对PD-1抗原抗体结合检测的实验研究[J]. 化学学报, 2019, 77(3): 287-292.
[9]	朱婵, 海洋, 赵志刚, 阳耀月. Ni和P微量掺杂的Pd基催化剂对碱性介质中乙醇电氧化性能的增强效应研究[J]. 化学学报, 2018, 76(1): 30-34.
[10]	陈方园, 曲宁, 吴群燕, 张红星, 石伟群, 潘清江. 二价双核铀聚吡咯配合物结构设计和铀-铀多重键的理论研究[J]. 化学学报, 2017, 75(5): 457-463.
[11]	杨晓东, 王新苗, 高善彬, 王安杰. Pd/ZSM-5/MCM-41催化剂加氢脱硫性能研究[J]. 化学学报, 2017, 75(5): 479-484.
[12]	李奇, 许瀚, 童叶翔, 李高仁. 高性能Pt纳米管中管电催化剂在甲醇燃料电池中的应用[J]. 化学学报, 2017, 75(2): 193-198.
[13]	赵思魏, 钟宇曦, 郭元茹, 张红星, 潘清江. 聚吡咯铀酰氧-酰亚胺配合物结构、振动光谱和基团交换反应的相对论密度泛函理论计算[J]. 化学学报, 2016, 74(8): 683-688.
[14]	黎聃勤, 张志琦, 臧鹏远, 马延文, 吴强, 杨立军, 陈强, 王喜章, 胡征. 介观结构氮掺杂碳纳米笼负载铂-钌合金催化剂的优异甲醇电氧化性能[J]. 化学学报, 2016, 74(7): 587-592.
[15]	冷明浩, 陈仕谋, 张军玲, 郎海燕, 康艳红, 张锁江. 含羰基有机添加剂对AlCl₃-[Emim]Cl电沉积铝的影响[J]. 化学学报, 2015, 73(5): 403-408.