Synthesis of NaY Zeolite on Sepiolite by in-situ Crystallization

Zheng Shuqin*,1 Han Yong1,2 Huang Shi1,2 Qian Dong2 Tang Kewen1 Yi Jianmin1   

  1. (1 Department of Chemistry and Chemical Engineering, Hunan Institute of Science and Technology, Yueyang 414000)
    (2 College of Chemistry and Chemical Engineering, Central South University, Changsha 410083)
  • Received:2009-07-01 Revised:2009-10-27 Published:2010-02-28

PDF

1346

Cited

2

A new approach for the synthesis of microporous molecular sieves was realized. The microporous NaY zeolite has been hydrothermally synthesized by in-situ crystallization using sepiolite as silica source and kaolin as aluminum source, and characterized by XRD and SEM. The effects of molar ratios of precursors and crystallization temperature were investigated. The crystallization temperature is the most important factor for the synthesis of zeolite NaY. The relative crystallinity of the samples markedly increased with crystallization temperature going up. When the reaction temperature increased up to 100 ℃, excellent zeolite crystals were obtained. The results showed that the relative crystallinity of NaY zeolite increased with the molar ratio of SiO2/Al2O3 declining. The increasing of molar ratio of Na2O/SiO2 and the decling of molar ratio of H2O/Na2O in the reaction system were favorable to the formation of NaY zeolite. It was found that the molar ratio of SiO2/Al2O3 played a dominant role in the molar ratios of precursors.

Key words: sepiolite, NaY, in-situ crystallization, synthesis