Synthesis of Supported TiO2/SBA-15 Catalysts and Their Performance on Photocatalytic Reduction of CO2

Wang Huixianga,b, Jiang Donga, Wu Donga, Li Debaoa, Sun Yuhana   

  1. a State Key Laboratory of Coal Conversion, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001;
    b University of Chinese Academy of Sciences, Beijing 100049
  • Received:2012-07-26 Published:2012-11-02
  • Supported by:
    Project supported by the National Natural Science Foundation of China (No. 21003150), the Natural Science Foundation of Shanxi Province (No. 2011011006-2) and Independent Research Foundation of the State Key Laboratory of Coal Conversion (No. 2011BWZ011).

以羧基改性的SBA-15 (COOH/SBA-15)和钛酸四丁酯(TB)为原料, 利用COOH/SBA-15表面上高分散的大量羧基将TB锚定, 通过溶剂热处理得到高分散负载型TiO2/SBA-15催化剂. 产物经XRD, Raman, FT-IR, TEM, N2吸脱附和UV-Vis表征, 结果显示: 所制备的TiO2/SBA-15催化剂为比表面大、结晶度较高的锐钛矿TiO2, TiO2均匀分散于SBA-15表面, 此外, COOH/SBA-15有效抑制了TiO2晶粒的长大. 以光催化还原CO2为探针反应, 考察了TiO2/SBA-15催化剂在紫外光照射下的光催化性能. 结果表明: 相比于后处理浸渍法制备的光催化剂, 本文制备的TiO2/SBA-15催化剂表现出了高的光催化还原CO2活性, 主要产物为甲醇, 且TiO2最佳负载量为16.5%, 并对相关反应机理做了探讨.

关键词: 羧基改性SBA-15, TiO2, 光催化还原CO2

TiO2/SBA-15 catalysts, TiO2 nanoparticles well dispersed on SBA-15 supporter, have been successfully obtained through a self-assembly aging, carboxylation and subsequent solvothermal process. Firstly, P123 (PEG-PPG-PEG), KCl, (2-cyanoethyl) triethoxysilane (CETES) and tetraethoxysilane (TEOS) were employed to form cyano-modified SBA-15 (CN/SBA-15) in 2.0 mol/L HCl solution by self-assembly aging method. Secondly, carboxyl-modified SBA-15 (COOH/SBA-15) was got through carboxylation treatment in 48% H2SO4 solution at 95℃ for 24 h. Finally, highly dispersed TiO2/SBA-15 catalysts were successfully synthesized via solvothermal method at 220℃ for 12 h using COOH/SBA-15 and tetrabutyl titanate (TB) as raw materials. In order to remove the organic compounds and improve the crystallization of TiO2, the obtained TiO2/SBA-15 catalysts then were filtrated, washed by absolute ethanol for three times, dried at 80℃ and calcined at 550℃ for 4 h. Notably, the self-assembly and carboxylation process produced large number of good dispersive carboxyl groups (COOH) on SBA-15, which could effectively anchored TB molecules on SBA-15 to promise the highly dispersion of TiO2 on SBA-15. The obtained TiO2/SBA-15 catalysts have been characterized by X-ray diffraction (XRD), Raman spectrum, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), nitrogen adsorption and UV-Visible diffuse reflectance spectroscopy (UV-Vis). Above results indicate that the TiO2/SBA-15 catalysts exhibit large specific surface area and TiO2 on SBA-15 supporter is anatase phase, they are both play important roles in photocatalytic application. In the current manuscript, the photocatalytic reduction of CO2 under UV light irradiation as a prober reaction was used to investigate the photocatalytic performance of TiO2/SBA-15 catalysts. It was found that the obtained catalysts performed high photocatalytic capacity for CO2 reduction, especially when the loading amount of TiO2 was around 16.5 wt% [n(COOH)/n(TB)=3], the methanol production got maximum which could reach 80 μmol/g-catalyst after 6 h UV light irradiation. Compared with the catalysts which synthesized through simple impregnation method, our TiO2/SBA-15 catalysts showed the higher activity in photocatalytic reduction of CO2, owing to the better dispersion and crystallization.

Key words: carboxyl-modified SBA-15, titanium dioxide, photocatalytic reduction of CO2