穆春辉a, 张艺馨a, 寇伟a, 徐联宾a,b,*()   

  1. a 北京化工大学有机无机复合材料国家重点实验室 北京 100029
    b 北京化工大学教育部超重力工程研究中心 北京 100029
  • 投稿日期:2021-03-22 发布日期:2021-06-25
  • 通讯作者: 徐联宾
  • 基金资助:
    国家自然科学基金(21676018)

Nickel-Nitrogen-Doped Ordered Macro-/Mesoporous Carbon Supported Ag Nanoparticles for Efficient Electrocatalytic CO2 Reduction

Chunhui Mua, Yixin Zhanga, Wei Koua, Lianbin Xua,b()   

  1. a State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China
    b Research Center of the Ministry of Education for High Gravity Engineering and Technology, Beijing University of Chemical Technology, Beijing 100029, China
  • Received:2021-03-22 Published:2021-06-25
  • Contact: Lianbin Xu
  • Supported by:
    National Natural Science Foundation of China(21676018)

多组分体系中的协同作用为设计高效的二氧化碳还原电催化剂提供了新的思路. 本工作通过双模板法和化学还原法精心设计制备了大孔/介孔镍氮掺杂碳(Ni-N-OMMC)负载银纳米颗粒复合材料(Ag/Ni-N-OMMC), 用于高效电催化还原CO2为CO. 此复合材料表现出良好的电催化活性, 在CO2饱和的0.1 mol•L–1 KHCO3电解液中, 电位为–1.0 V (相对于可逆氢电极, RHE)时CO的电流密度(JCO)高达33.29 mA•cm–2. 并具有较宽的工作电压范围, 在–0.7~–1.0 V (vs. RHE)下, CO的法拉第效率超过90%. 其优异的电催化性能可能归因于Ag纳米颗粒与具有丰富Ni-N x活性位点的Ni-N-OMMC载体之间的协同效应, 以及三维互联有序大孔/介孔结构提供的高比表面积和高效的质量/电荷传输.

关键词: 有序大孔/介孔结构, 镍氮共掺杂碳, 双模板合成, 银纳米颗粒, 电催化CO2还原

Electrocatalytic CO2 reduction (ECR) into high value-added chemical products has been regarded as an effective strategy to release environmental crisis caused by high concentration of CO2 in the atmosphere, because of its mild operation conditions and the ability to use renewable energy sources as power. Metal-nitrogen-doped carbon-based nanomaterials have been demonstrated as excellent catalysts for electrochemical reduction of CO2 due to their high selectivity and low cost. However, it suffers from the problem of low Faradaic efficiency at high current density, which limits their further applications. In addition, the silver-based catalysts have good catalytic activity for the electrochemical reduction of CO2 to CO, but they can only achieve high selectivity under high overpotentials. The synergistic effect in the multi-component system provides a new idea for the design of efficient electrocatalysts for carbon dioxide reduction. Herein, we first elaborately design and prepare an ordered macro-/mesoporous nickel-nitrogen-doped carbon (Ni-N-OMMC) supported silver nanoparticles composite (Ag/Ni-N-OMMC) by the use of silica colloidal crystal as the hard template and triblock copolymer Pluronic F127 as the mesoporous structure-directing agent, and study the electrocatalytic CO2 reduction performance. Due to the confinement effect, the small silver nanoparticles are successfully loaded on the Ni-N-OMMC support by in-situ chemical reduction. Compared to Ni-N-OMMC, Ag/Ni-N-OMMC exhibits better electrocatalytic activity. The Faradaic efficiency of CO is as high as 98.7% when the potential is –0.7 V vs. reversible hydrogen electrode (RHE) in 0.1 mol•L–1 KHCO3 electrolyte. Moreover, Ag/Ni-N-OMMC has a wide operating voltage range with the Faradaic efficiency of CO over 90% at –0.7~ –1.0 V, and shows a high current density of CO (33.29 mA•cm–2) at –1.0 V. The excellent ECR performance of Ag/Ni-N-OMMC may be attributed to the synergistic effect between Ag nanoparticles and the Ni-N-OMMC support with abundant Ni-N x active sites, as well as the high specific surface area and efficient mass/charge transfer provided by the three-dimensional interconnected ordered macro-/mesoporous structure. This study provides an idea for future design and preparation of metal-carbon composite electrocatalysts with high activity and selectivity.

Key words: ordered macro-/mesoporous structure, Ni-N-doped carbon, dual-templating synthesis, Ag nanoparticle, electrocatalytic CO2 reduction