Hydrothermal Synthesis of MoS2/CNT Coaxial Nanotubes

XIA Jun-Bao¹, XU Zhu-De¹, CHEN Wei-Xiang¹, ZHENG Yi-Fan^1,2, DU Zhi-Qiang¹

1. Department of Chemistry, Zhejiang University, Hangzhou 310027;
2. College of Chemical Engineering and Materials, Zhejiang University of Technology, Hangzhou 310014

Received:2003-11-25 Revised:2004-05-19 Published:2014-02-17

文章分享

摘要/Abstract

采用水热法合成了MoS₂/CNT同轴纳米管.对合成的MoS₂/CNT同轴纳米管用高分辨透射电镜(HRTEM)、X射线衍射(XRD)和电子能谱(EDS)方法对其进行了鉴定和表征,发现所制备的MoS₂/CNT同轴纳米管结构完好,在CNT的外表面包覆了3～4层MoS2管.初步分析了MoS₂/CNT的形成机理.

关键词: 纳米管, 二硫化钼, 碳纳米管, 一维复合材料

MoS₂/CNT coaxial nanotubes were successfully synthesized by a hydrothermal method. The high-resolution transmission electron microscopy (HRTEM) and X-ray diffraction (XRD) were used to characterize MoS₂/CNT coaxial nanotubes. It showed that CNT was uniformly coated with three to four layers of MoS₂. The formation mechanism of the MoS₂/CNT was discussed.

Key words: nanotube, MoS₂,carbon nanotube,one2dimension composite

引用此文

夏军保, 徐铸德, 陈卫祥, 郑遗凡, 杜志强. 水热法合成MoS₂/CNT同轴纳米管[J]. 化学学报, 2004, 62(20): 2109-2112.

XIA Jun-Bao, XU Zhu-De, CHEN Wei-Xiang, ZHENG Yi-Fan, DU Zhi-Qiang. Hydrothermal Synthesis of MoS2/CNT Coaxial Nanotubes[J]. Acta Chimica Sinica, 2004, 62(20): 2109-2112.

导出引用 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

分享此文

参考文献

[1] Iijima, S. Nature 1991, 354, 8.
[2] Kondo, Y.; Takayanagi, K. Science 2000, 289, 606.
[3] Blase, X.; Charlier, J. C.; De Vita, A.; Car, R. Appl.Phys. A 1999, 68, 293.
[4] Zhang, Y.; Suenaga, K.; Colliex, C.; Iijima, S. Science 1998,281, 973.
[5] Chun, S. Y.; Chayahara, A.; Horino, Y. Appl. Surf. Sci.2001, 169, 607.
[6] Shen, G. Z.; Chen, D.; Tang, K. B.; Qian, Y. T.; Zhang,S. Y. Chem. Phys. Lett. 2003, 375, 177.
[7] Li, Q. Q.; Fan, S. H.; Han, W. Q.; Sun, C. H.; Liang,W. J. Jpn. J. Appl. Phys. 1997, 36, 501.
[8] Ang, L. M.; Hor, T. S. A.; Xu, G. Q.; Tung, C. H.;Zhao, S. P.; Wang, J. L. S. Carbon 2000, 38, 363.
[9] Zhang, Y. J.; Zhang, Q.; Li, Y. B.; Wang, N. L.; Zhu, J.Solid State Commun. 2000, 115, 51.
[10] Sloan, J.; Cook, J.; Heesom, J. R.; Green, M. L. H.;Hutchison, J. L. J. Cryst. Growth 1997, 173, 81.
[11] Tsang, S. C.; Chen, Y. K.; Harris, P. J. F.; Green, M. L.H. Nature 1994, 372, 159.
[12] Ajayan, P. M.; Iijima, S. Nature 1994, 361, 333.
[13] Stelur, A. A.; Lauerhaas, J. M.; Dai, J. Y.; Chang, R.;Zhang, P. H. Appl. Phys. Lett. 1996, 69, 345.
[14] Tenne, R.; Margulis, L.; Genut, M.; Hodes, G. Nature 1992,360, 444.
[15] Margulies, L.; Salitra, G.; Tenne, R.; Talianker, M. Nature1993, 365, 113.
[16] Whitby, R. L. D.; Hsu, W. K.; Bothroyd, C. B.; Fearon, P.K.; Kroto, H. W.; Walton, D. R. M. Chem. Phys. Chem.2001, 10, 620.
[17] Whitby, R. L. D.; Hsu, W. K.; Fearon, P. K.; Billingham,N. C.; Maurin, I.; Kroto, H. W.; Walton, D. R. M.;Boothroyd, C. B.; Firth, S.; Clark, R. J. H.; Collison, D.Chem. Mater. 2002, 14, 2209.
[18] Whitby, R. L. D.; Hsu, W. K.; Watts, P. C. P.; Kroto, H.W.; Walton, D. R. M.; Boothroyd, C. B. Appl. Phys. Lett.2001, 79, 4574.
[19] Hsu, W. K.; Zhu, Y. Q.; Kroto, H. W.; Walton, D. R.M.; Kamalakaran, R.; Terrones, M. Appl. Phys. Lett. 2000,77, 4130.
[20] Zhu, Y. Q.; Hsu, W. K.; Kroto, H. W.; Walton, D. R. M.Chem. Commun. 2001, 21, 2184.
[21] Chen, J.; Li, S. L.; Gao, F; Xu, Q.; Tanaka, K. Sci.China, Ser. B 2003, 46, 191.
[22] Frey, G. L.; Tenne, R.; Matthews, M. J.; Dresselhaus, M.S.; Dresselhaus, G. J. Mater. Res. 1998, 13, 2412.
[23] Bokhimi, X.; Toledo, J. A.; Navarrete, J.; Sun, X. C.;Portilla, M. Int. J. Hydrogen Energ. 2001, 26, 1271.
[24] Yu, S. H.; Han, Z. H.; Yang, J. Chem. Mater. 1999, 11,192.

水热法合成MoS₂/CNT同轴纳米管

Hydrothermal Synthesis of MoS2/CNT Coaxial Nanotubes

PDF

可视化

摘要/Abstract

引用此文

分享此文

参考文献

相关文章 15

编辑推荐

相关统计

本文评价

[1]	赵天成, 蒋鸿宇, 张琨, 徐一帆, 康欣悦, 胥鉴宸, 周旭峰, 陈培宁, 彭慧胜. 基于环烷烃/乙醇混合碳源高性能碳纳米管纤维的连续化制备[J]. 化学学报, 2023, 81(6): 565-571.
[2]	刘稳, 王昱捷, 杨慧琴, 李成杰, 吴娜, 颜洋. 离子液体非共价诱导制备碳纳米管/石墨烯集流体用于钠金属负极[J]. 化学学报, 2023, 81(10): 1379-1386.
[3]	成受明, 周波. 基于超高分辨质谱的溶解性有机质分子转化机理分析[J]. 化学学报, 2022, 80(8): 1106-1114.
[4]	王超峰, 郑国栋, 王悦, 宋慧佳, 陈小艺, 高瑞霞. 金属卟啉-Sn网络可控非共价功能化碳纳米管的制备及蛋白吸附应用[J]. 化学学报, 2022, 80(2): 126-132.
[5]	张欣欣, 刘荣, 王蕾, 付宏刚. 细菌纤维素基柔性锌离子电池正极的构筑及性能研究[J]. 化学学报, 2021, 79(5): 670-677.
[6]	崔丽瑞, 张劲, 孙一焱, 卢善富, 相艳. 碳纳米管添加剂对质子交换膜燃料电池低铂载量膜电极性能的影响研究[J]. 化学学报, 2019, 77(1): 47-53.
[7]	朱明晶, 彭娟, 唐萍, 邱枫. 高稳定性和水溶性的共轭聚电解质/单壁碳纳米管复合物的制备和表征[J]. 化学学报, 2018, 76(6): 453-459.
[8]	张田, 郭琛, 魏淑贤, 武中华, 韩兆翔, 鲁效庆. 甲硫醇在Co修饰MoS₂团簇边缘位的脱硫机理研究[J]. 化学学报, 2018, 76(1): 62-67.
[9]	李磊, 贾桂霄, 王晓霞, 吴铜伟, 宋希文, 安胜利. 基于缺陷曲率对含有V₁~V₄空位(5,5)单壁碳纳米管[1+1]和[2+1]加成反应的第一性原理研究[J]. 化学学报, 2017, 75(3): 284-292.
[10]	陈鑫, 鄢慧君, 夏定国. 锗纳米管催化的氧还原反应:催化性能和机理研究[J]. 化学学报, 2017, 75(2): 189-192.
[11]	周智伟, 李庆威, 陈鲁倬, 刘长洪, 范守善. 一种基于碳纳米管/高分子复合材料的流量控制致动器[J]. 化学学报, 2016, 74(9): 738-743.
[12]	王雷, 李雪, 郑斐, 郭玉鑫, 张志强, 迟海军, 董岩, 王翠苹, 卢公昊. 自组装金属有机纳米管模板法制备高分子纳米管[J]. 化学学报, 2016, 74(3): 259-264.
[13]	赵秘, 李浩华, 沈小平. 电化学沉积法制备CeO₂@Ag@CdSe纳米管阵列及其光电化学性能研究[J]. 化学学报, 2016, 74(10): 825-832.
[14]	史建平, 马冬林, 张艳锋, 刘忠范. 金箔上单层MoS₂的控制生长及电催化析氢应用[J]. 化学学报, 2015, 73(9): 877-885.
[15]	沈成, 张菁, 时东霞, 张广宇. 退火对单层二硫化钼荧光特性的影响[J]. 化学学报, 2015, 73(9): 954-958.