化学学报 ›› 2003, Vol. 61 ›› Issue (2): 151-155.    下一篇

研究论文

烯丙基硫脲和十二烷基硫醇对铜的缓蚀作用

王春涛;陈慎豪;赵世勇;李德刚   

  1. 山东大学化学与化工学院
  • 发布日期:2003-02-15

Inhibition Effect of Allylthiourea and 1-Dodecanethiol on Copper Corrosion

Wang Chuntao;Chen Shenhao;Zhao Shiyong;Li Degang   

  1. School of Chemistry and Chemical Engineering,Shandong University
  • Published:2003-02-15

PDF

1185

被引次数

66 | 10

用自组装技术在铜电极表面上制备了纯烯丙基硫服自组装膜，并以十二烷基硫 醇进一步修饰得到混合自组装膜。最后，将混合膜覆盖的铜电极浸入NaCl溶液中， 进行交流电处理，电化学交流阻抗谱和极化曲线测定表明，经过交流电处理后，在 0．5mol·dm^-3 NaCl溶液中，电荷传递电阻增大，腐蚀电流密度下降，膜的最大 覆盖度为98．6％，对金属铜腐蚀的续蚀效率为98．5％。而且，不论交流电处理与 否，混合自组装膜在较宽的电极电位范围内均表现出很强的稳定性。

关键词: 硫脲 P, 硫醇, 稳定性, 阻抗, 腐蚀

Self-assembled monolayer of allylthiourea (AT) was first formed on copper surface. 1-Dodecanethiol (DT) was then self-assembled on ihe surface for subsequent modification. Finally, AC voltage was loaded on copper covered with the mixed film for further improvement. After these processes, an effective inhibition film was obtained as indicated by the high charge-transfer resistance shown in electrochemical impedance spectroscopy and low corrosion current density in polarization curves. The maximum coverage and inhibition efficiency for copper corrosion was 98.6 % and 98.5%, respectively. The mixed film was stable in a wide range of potential before and after AC voltage treatment

Key words: THIOUREA P, MERCAPTAN, STABILITY, IMPEDANCE, CORROSION