非晶态合金作催化材料的研究IV. 超细非晶态Ni-B催化剂的制备及催化性能研究

杨军;柴亮;邓景发;赵慧玲   

  1. 复旦大学化学系;复旦大学分析测试中心电镜室
  • 发布日期:1994-01-15

Studies of amorphous metals as catalytic material IV. perparation of amorphous Ni-B ultrafine particles and its catalytic properties

YANG JUN;CHAI LIANG;DENG JINGFA;ZHAO HUILING   

  • Published:1994-01-15

采用化学还原法制备了非晶态Ni-B超细粒子催化剂, 所含两种粒子的粒径分别为5~20nm和150nm左右。对环戊二烯常压液相加氢反应的活性测试结果表明, 该催化剂具有很高的活性和选择性, 并且在加氢反应中具有替代Raney Ni和Pd/C催化剂的工业应用潜力。动力学测量表明, 在该催化剂上, 环戊二烯选择加氢生成环戊烯的反应为零级, 环戊烯生成环戊烷的反应为近似一级。

关键词: 催化, 催化剂, 镍, 环戊二烯, 硼, 超细粒子, 非晶态合金

The amorphous Ni-B ultrafine particles were prepared by using KBH~4 to reduce Ni^2+ ion in ethanol solution, and two kinds of particles with the average diameter around 150nm and 5~25nm respectively were observed. The hydrogenation of 1, 3-cyclopentadiene were also investigated by using these particles, and a higher hydrogenation activity and selectivity of cyclopentene were observed. As a comparation, Raney Ni and Pd/C catalysts were also used to catalyze the same reaction. The results show thatamorphous Ni-B ultrafine particles display to have a higher catalytic hydrogenation ability and can be used in the reaction of hydrogenation instead of Raney Ni and Pd/C catalysts.

Key words: CATALYSIS, CATALYST, NICKEL, CYCLOPENTADIENE, BORON, MICRO-SIZE PARTICLES, AMORPHOUS ALLOY