Ultrasonic Synthesis of pH-Sensitive PMAA Hydrogel

Liu Weitaoa, Liu Xuewena, Zhu Shena, Liu Xinyia, Han Guozhia,b   

  1. a Department of Applied Chemistry, College of Science, Nanjing University of Technology, Nanjing 210009;
    b State Key Laboratory of Bioelectronics, Southeast University, Nanjing 210096
  • Received:2011-07-26 Revised:2011-09-09 Published:2011-10-09
  • Supported by:

    Project was supported by the China Postdoctoral Science Foundation (No. 20100481084) and Jiangsu Province Postdoctoral Science Foundation (No. 1002006C).

PDF

2421

Cited

13 | 8

Using methacrylic acid as starting materials, N,N'-methylene bisacrylamide as a crosslinker and potassium persulfate as initiator, pH sensitive poly(methacrylic acid) (PMAA) hydrogel was synthesized by free radical polymerization under ultrasonic radiation. The molecular structure and chemical properties of hydrogel were characterized by IR and SEM. On this basis, impact of ultrasonication on swelling-deswelling of hydrogel was emphatically studied. Experimental results indicated that intelligent hydrogels prepared by ultrasonic synthesis have higher equilibrium swelling ratio and faster response comparing to traditional methods.

Key words: ultrasonic, pH sensitive, poly(methacrylic acid) (PMAA), hydrogel, synthesis