Porous Perovskite towards Oxygen Reduction Reaction in Flexible Aluminum-Air Battery

doi:10.6023/A20030068

Acta Chimica Sinica ›› 2020, Vol. 78 ›› Issue (6): 557-564.DOI: 10.6023/A20030068 Previous Articles Next Articles

Article

多孔钙钛矿型氧还原催化剂在柔性铝空气电池中的应用研究

税子怡^a, 何娜娜^a, 陈黎^a, 赵炜^a, 陈曦^a,b

a 西北大学化工学院西安 710069;
b 哥伦比亚大学地球与环境学院能源环境先进材料研究中心纽约 NY10027

投稿日期:2020-03-14 发布日期:2020-05-19
通讯作者: 赵炜, 陈曦 E-mail:zhaowei3313@nwu.edu.cn;xichen863@hotmail.com
基金资助:
项目受国家自然科学基金（No.11872302）、陕西省自然科学基础研究计划（No.2019JQ-431）和陕西省教育厅自然科学专项（No.20JK0927）资助.

Porous Perovskite towards Oxygen Reduction Reaction in Flexible Aluminum-Air Battery

Shui Ziyi^a, He Nana^a, Chen Li^a, Zhao Wei^a, Chen Xi^a,b

a Northwest University, School of Chemical Engineering, Xi'an 710069;
b Columbia University, Department of Earth and Environmental Engineering, New York NY 10027

Received:2020-03-14 Published:2020-05-19
Supported by:
Project supported by the National Natural Science Foundation of China (No. 11872302), the Natural Science Basic Research Program of Shaanxi Province (No. 2019JQ-431) and the Shaanxi Provincial Department of Education Natural Science Special Project (No. 20JK0927).

Perovskite-type catalytic materials have received wide attention as high-performance and low-cost alternatives to precious metal catalysts on the market at present, which have much considerable activity and stability as catalysts for oxygen reduction reactions. Current efforts are mainly focused on the use of perovskite make-up and preparation techniques to influence elemental composition, morphology, surface area, and structural control. For a typical perovskite oxide (ABO₃), due to the high calcination temperature in the preparation process, the perovskite material usually has a small specific surface area, which limits the increase of activity in heterogeneous catalytic reactions. In this paper, the perovskite La_0.7Sr_0.3MnO₃ (LSMO) material with large specific surface and high catalytic activity is prepared by means of the SiO₂ template. The physicochemical properties of the synthesized materials are characterized by scanning electron microscope (SEM), energy dispersed X-ray spectroscopy (EDS), X-ray diffraction (XRD) and BET. The catalytic activity of LSMO as an oxygen reduction reaction (ORR) catalyst is measured by a rotating disk test system. After that, the catalyst material is applied to a flexible aluminum-air battery and its discharge behavior and flexibility is studied and tested. The test results show that the LSMO prepared by template method has a large specific surface area (31.1825 m²·g^-1), and pore volume (0.161113 cm³·g^-1), and it also shows higher electrocatalytic activity in the electrochemical test system. When it is used in aluminum-air batteries, the activity of 3D porous LSMO is significantly better than that of sheet and bulk LSMO. The aluminum-air battery assembled by LSMO prepared by the template method has a higher discharge voltage (up to 1.46 V) at a constant current. Compared to the template-free method and the sol-gel method, the discharge voltage in flexible aluminum-air battery can be increased by 8.2% and 24.5%, respectively, and the performance degradation is significantly slowed during high-current discharge. The specific capacity and energy density of the battery are up to 1048.6 mA·h·g^-1 and 1020.6 mW·h·g^-1, respectively. When the battery is in a deformed state, its output voltage can be stabilized above 1.38 V. Once released, the voltage can be immediately restored to over 99% of the initial value. This paper not only provides a solution for the commercialization of fuel cell, but also provides a new direction for the future development of variable power supply.

Key words: perovskite oxide, specific surface area, oxygen reduction reaction, catalytic activity, flexible aluminum-air battery

Cite this article

Shui Ziyi, He Nana, Chen Li, Zhao Wei, Chen Xi. Porous Perovskite towards Oxygen Reduction Reaction in Flexible Aluminum-Air Battery[J]. Acta Chimica Sinica, 2020, 78(6): 557-564.

Export EndNote|Reference Manager|ProCite|BibTeX|RefWorks

share this article

References

[1] Song, M. J.; Shin, M. W. Appl. Surf. Sci. 2014, 320, 435.
[2] Arora, P.; Zhang, Z. J. Chem. Rev. 2004, 104, 4419
[3] Xu, Y.; Zhao, Y.; Ren, J.; Zhang, Y.; Peng, H. Angew. Chem., Int. Ed. 2016, 55, 7979.
[4] Que, Y.; Qi, M.; Shi, P. Chin. Battery Ind. 2019, 23, 147. (阙奕鹏, 齐敏杰, 史鹏飞, 电池工业, 2019, 23, 147.)
[5] Xie, K.; Wei, B. Adv. Mater. 2014, 26, 3592.
[6] Cheng, F.; Chen, J. Chem. Soc. Rev. 2012, 41, 2172.
[7] Cheng, F.; Chen, J. Acta Chim. Sinica 2013, 71, 473. (程方益, 陈军, 化学学报, 2013, 71, 473.)
[8] Hong, Q.; Lu, H. Sci. Rep. 2017, 7, 3378.
[9] Li, Y. C.; Xu, Z. C.; Gasteiger, H. A.; Chen, S.; Hamad-Schifferli, K.; Yang, S.-H. J. Am. Chem. Soc. 2010, 132, 12170.
[10] Meng, H.; Shen, P. K. Electrochem. Commun. 2006, 8, 588.
[11] Hao, J.; Liu, Y.; Li, W.; Li, J. Mater. Rev. 2019, 33, 127. (郝佳瑜, 刘易斯, 李文章, 李洁, 材料导报, 2019, 33, 127.)
[12] Jin, Q.; Pei, L.; Hu, Y.; Du, J.; Han, X.; Cheng, F.; Chen, J. Acta Chim. Sinica 2014, 72, 920. (靳琪, 裴龙凯, 胡宇翔, 杜婧, 韩晓鹏, 程方益, 陈军, 化学学报, 2014, 72, 920.)
[13] Wang, D.; Chen, X.; Evans, D.-G.; Yang, W. Nanoscale 2013, 5, 5312.
[14] Wang, Y.; Wei, Z. J. Electrochem. 2018, 24, 427. (王尧, 魏子栋, 电化学, 2018, 24, 427.)
[15] Yin, W.; Shen, Y.; Zou, F.; Hu, X.; Chi, B.; Huang, Y. ACS Appl. Mater. Interfaces 2015, 7, 4947.
[16] Liu, M.; Zhang, R.; Chen, W. Chem. Rev. 2014, 114, 5117.
[17] Liu, L.; Yuan, Z.; Qiu, C.; Liu, J. Solid State Ionics 2013, 241, 25.
[18] Wang, Y.; Zhang, L.; Hu, T. Acta Chim. Sinica 2015, 73, 316. (王瀛, 张丽敏, 胡天军, 化学学报, 2015, 73, 316.)
[19] Miyazaki, K.; Kawakita, K.; Abe, T.; Fukutsuka, T.; Kojima, K.; Ogumi, Z. J. Mater. Chem. 2011, 21, 1913.
[20] Lin, S.; Xu, S.-F.; Wang, J.-D.; Xie, C.-S.; Yuan, A.-H.; Han, G.-F.; Zhang, L.; Zhang, L.-M.; Li, Y.; Yan, Z.-M. Acta Chim. Sinica 2005, 63, 385. (林生岭, 徐绍芬, 王俊德, 谢春生, 袁爱华, 韩光范, 张琳, 张黎明, 李燕, 严豸明, 化学学报, 2005, 63, 385.)
[21] Takeguchi, T.; Yamanaka, T.; Takahashi, H.; Watanabe, H.; Kuroki, T.; Nakanishi, H.; Orikasa, Y.; Uchimoto, Y.; Takano, H.; Ohguri, N.; Matsuda, M.; Murota, T.; Uosaki, K.; Ueda, W. J. Am. Chem. Soc. 2013, 135, 11125.
[22] Xue, Y.; Miao, H.; Sun, S.; Wang, Q.; Li, S.; Liu, Z. J. Power Sources 2017, 342, 192.
[23] Stoerzinger, K. A.; Lü, W.; Li, C.; Ariando; Venkatesan, T.; Yang, S.-H. J. Phys. Chem. Lett. 2015, 6, 1435.
[24] Hu, J.; Wang, L.; Shi, L.; Huang, H. J. Power Sources 2014, 269, 144.
[25] Liu, Y.; Dai, H.; Du, Y.; Deng, J.; Zhang, L.; Zhao, Z.; Au, C. T. J. Catal. 2012, 287, 149.
[26] Lee, Y. C.; Peng, P. Y.; Chang, W. S.; Huang, C. M. J. Taiwan Chem. Eng. 2014, 45, 2334.
[27] Stöber, W.; Fink, A.; Bohn, E. J. Colloid Interface Sci. 1968, 26, 62.
[28] Yang, C. H.; Chen, B. J.; Lu, J.; Yang, J. H.; Zhou, J.; Chen, Y. M.; Suo, Z. Extreme Mech. Lett. 2015, 25, 59.
[29] Tan, P.; Chen, B.; Xu, H.; Zhang, H.; Cai, W.; Ni, M.; Liu, M.; Shao, Z. Energy Environ. Sci. 2017, 10, 2056.
[30] Song, S.-D.; Tang, Z.-Y.; Pan, L.-Z.; Nan, J.-M. Acta Chim. Sinica 2005, 63, 363. (宋世栋, 唐致远, 潘丽珠, 南俊民, 化学学报, 2005, 63, 363.)
[31] Liu, Y.; Li, J.; Li, W.; Li, Y.; Zhan, F.; Tang, H.; Chen, Q. Int. J. Hydrogen Energy 2016, 41, 10354.
[32] Zhang, Z.; Zuo, C.; Liu, Z.; Yu, Y.; Zuo, Y.; Song, Y. J. Power Sources 2014, 251, 470.

多孔钙钛矿型氧还原催化剂在柔性铝空气电池中的应用研究

Porous Perovskite towards Oxygen Reduction Reaction in Flexible Aluminum-Air Battery

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Ping Li, Qiyu Yang, Jing Zeng, Ran Zhang, Qiuyan Chen, Fei Yan. Effect of Fluorine Doping on the Performance of Reversible Solid Oxide Cells and Related Kinetic Studies [J]. Acta Chimica Sinica, 2024, 82(1): 36-45.
[2]	Qiwen Chen, Xianzheng Zhang. Reserach Advances on Nanozyme-Guided Therapy of Inflammatory Bowel Diseases^★ [J]. Acta Chimica Sinica, 2023, 81(8): 1043-1051.
[3]	Jinjing Liu, Na Yang, Li Li, Zidong Wei. Theoretical Study on the Regulation of Oxygen Reduction Mechanism by Modulating the Spatial Structure of Active Sites on Platinum^★ [J]. Acta Chimica Sinica, 2023, 81(11): 1478-1485.
[4]	Shaobing Yan, Long Jiao, Chuanxin He, Hailong Jiang. Pyrolysis of ZIF-67/Graphene Composite to Co Nanoparticles Confined in N-Doped Carbon for Efficient Electrocatalytic Oxygen Reduction [J]. Acta Chimica Sinica, 2022, 80(8): 1084-1090.
[5]	Dan Wang, Bo Feng, Xiaoxin Zhang, Yanan Liu, Yan Pei, Minghua Qiao, Baoning Zong. Nitrogen-doped Carbon Pyrolyzed from ZIF-8 for Electrocatalytic Oxygen Reduction to Hydrogen Peroxide [J]. Acta Chimica Sinica, 2022, 80(6): 772-780.
[6]	Lu Xiaoqing, Cao Shoufu, Wei Xiaofei, Li Shaoren, Wei Shuxian. Investigation on Oxygen Reduction Reaction Mechanism on S Doped Fe-NC lsolated Single Atoms Catalyst [J]. Acta Chimica Sinica, 2020, 78(9): 1001-1006.
[7]	Wu Yan, Pang Aimin, Hu Lei, He Gensheng, Zhang Yingying, Zhang Lixiong, Li Minghai, Ma Zhenye. Preparation of α-Fe₂O₃/(IPDI-HTPB) Composite Nanoparticles and Their Catalytic Performance [J]. Acta Chimica Sinica, 2020, 78(4): 337-343.
[8]	Li Wei, Ran Tiecheng, Zhang Yu, He Wei, Ma Jifei, Wang Qisheng, Zhang Jichao, Zhu Ying. SiO₂-Mediated High-efficiency Enrichment of 5 nm Gold Nanoparticles and Their Catalytic Activity [J]. Acta Chimica Sinica, 2020, 78(2): 170-176.
[9]	Huang Wenjiao, Zhang Haoyu, Hu Shuozhen, Niu Dongfang, Zhang Xinsheng. Effect of Nitrogen-Containing Functional Groups of Cobalt Phthalocyanine Catalyst on the Oxygen Reduction Performance in Fuel Cells [J]. Acta Chim. Sinica, 2018, 76(9): 723-728.
[10]	Chu Wanyi, Tang Xiao, Li Zhen, Lin Jingcheng, Qian Jueshi. Influence Factors on the Microstructure of Ultrathin TiO₂ Nanosheets Synthesized by Liquid Phase Method [J]. Acta Chim. Sinica, 2018, 76(7): 549-555.
[11]	Chen Xin, Yan Huijun, Xia Dingguo. Germanium Nanotube as the Catalyst for Oxygen Reduction Reaction: Performance and Mechanism [J]. Acta Chim. Sinica, 2017, 75(2): 189-192.
[12]	Zhong Guoyu, Wang Hongjuan, Yu Hao, Peng Feng. A Review of Carbon-based Non-noble Catalysts for Oxygen Reduction Reaction [J]. Acta Chim. Sinica, 2017, 75(10): 943-966.
[13]	Niu Dongfang, Ding Yong, Ma Zhixing, Wang Minghui, Liu Zhou, Zhang Bowen, Zhang Xinsheng. Effects of Surface Modification of Carbon Nanofibers on Their Electro- catalytic Activity for Hydrogen Evolution Reaction of Water Electrolysis [J]. Acta Chim. Sinica, 2015, 73(7): 729-734.
[14]	Wan Gang, Fu Yu'ang, Guo Jianing, Xiang Zhonghua. Photoelectronic Porous Covalent Organic Materials: Research Progress and Perspective [J]. Acta Chim. Sinica, 2015, 73(6): 557-578.
[15]	Wang Ying, Zhang Limin, Hu Tianjun. Progress in Oxygen Reduction Reaction Electrocatalysts for Metal-Air Batteries [J]. Acta Chim. Sinica, 2015, 73(4): 316-325.