TiO2/蒙脱石层间化合物的制备及层间原位反应过程研究

孙红娟*,1,2，彭同江1,2，陈彦翠1，古朝建1   

  1. (1西南科技大学固体废物处理与资源化省部共建教育部重点实验室 绵阳 621010)
    (2西南科技大学矿物材料及应用研究所 绵阳 621010)
  • 投稿日期:2010-11-26 修回日期:2011-01-25 发布日期:2011-05-03
  • 通讯作者: 孙红娟 E-mail:sunhongjuan@swust.edu.cn
  • 基金资助:

    国家自然科学基金;国家支撑计划项目

Interlayer in-situ Reaction Process and Preparation of TiO2/montmorillonite Composites

Sun Hongjuan*,1,2 Peng Tongjiang1,2 Chen Yancui1 Gu Chaojian1   

  1. (1 Key Laboratory of Solid Waste Treatment and Resource Recycle Ministry of Education, Southwest University of Science and Technology, Mianyang 621010)
    (2 Institute of Mineral Materials & Application, Southwest University of Science and Technology, Mianyang 621010)
  • Received:2010-11-26 Revised:2011-01-25 Published:2011-05-03
  • Contact: SUN Hong-Juan E-mail:sunhongjuan@swust.edu.cn

PDF

1088

基于蒙脱石层间域的二维纳米反应器属性, 通过溶剂化作用, 将氧化钛前躯体钛酸丁酯引入有机季铵盐阳离子插层的蒙脱石层间域中, 并使其在蒙脱石层间域中水解、成核和相变结晶. 采用XRD、原位升温Raman光谱、TEM分析手段研究了钛酸丁酯进入蒙脱石层间域过程, 以及钛酸丁酯在蒙脱石层间域中水解和TiO2成核及相转变过程. 结果表明钛酸丁酯成功进入了蒙脱石的层间域中, 进入的量随作用时间的增加而增大|钛酸丁酯在蒙脱石层间域中水解生成无定形水合氧化钛, 在150 ℃时开始形成锐钛矿结构的晶核, 当焙烧温度达到500 ℃时, TiO2晶核结晶生成非常有序的锐钛矿结构|当焙烧温度达到700 ℃时, 锐钛矿结构开始相转变为金红石结构, 当温度达到1200 ℃时, 锐钛矿相TiO2全部消失转变为金红石相TiO2.

关键词: 蒙脱石, 二氧化钛, 溶剂化作用, 水解过程, 相转变过程

Based on the two dimensional nanometer-reactor properties of interlayer spacing of montmorillonite, tetrabutyl titanate was introduced into the interlayer spacing of organic montmorillonite by solvent process. TiO2 was formed by using the interlayer spacing of montmorillonite as the reaction space. X-ray diffraction (XRD), in situ temperature Raman spectroscopy and TEM were used to analyze the reaction and hydrolyzation process of tetrabutyl titanate, the process of nucleation and structural phase transition of TiO2 in the interlayer spacing of montmorillonite. The results showed that tetrabutyl titanate was successfully introduced into the interlayer space of montmorillonite. The amount of tetrabutyl titanate entering into the interlayer of montmorillonite increased with the adsorption time increasing. The tetrabutyl titanate hydrolyzed into amorphous hydrated titania in the interlayer of montmorillonite. Hydrated titania in the interlayer of montmorillonite began to form crystal nucleus which was anatase TiO2 structural crystal nucleus at 150 ℃. When the baking temperature up to 500 ℃, the TiO2 crystal nucleus crystallized into complete ordering anatase. The anatase was gradually transformed to rutile at the temperature of 700 ℃. The anatase phase was transformed to rutile phase completely with the baking temperature up to 1200 ℃.

Key words: montmorillonite, TiO2, solvent action, hydrolyzation process, phase transition process