锗酸锌纳米棒@石墨烯复合负极材料的制备及储锂性质

doi:10.6023/A15100658

化学学报 ›› 2016, Vol. 74 ›› Issue (2): 185-190.DOI: 10.6023/A15100658 上一篇下一篇

研究论文

锗酸锌纳米棒@石墨烯复合负极材料的制备及储锂性质

童震坤, 方姗, 郑浩, 张校刚

江苏省能量转换材料与技术重点实验室南京航空航天大学材料科学与技术学院南京 211106

投稿日期:2015-10-14 发布日期:2016-01-29
通讯作者: 张校刚 E-mail:azhangxg@nuaa.edu.cn
基金资助:
项目受国家重点基础研究发展计划(973项目)(No.2014CB239701)、国家自然科学基金(Nos.21173120,51372116)、江苏省自然科学基金(BK2011030)和中央高校基本科研业务费专项资金(NP2014403,NJ20140004)和江苏高校优势学科建设工程项目资助.

Zn₂GeO₄ Nanorods@Graphene Composite as Anode Materials for Li-ion Batteries

Tong Zhenkun, Fang Shan, Zheng Hao, Zhang Xiaogang

Jiangsu Key Laboratory of Materials and Technology for Energy Conversion, College of Material Science and Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 211106

Received:2015-10-14 Published:2016-01-29
Supported by:
Project supported by the National Basic Research Program of China (973 Program) (No. 2014CB239701), the National Natural Science Foundation of China (Nos. 21173120, 51372116), the Natural Science Foundation of Jiangsu Province (BK2011030), the Fundamental Research Funds for the Central Universities of NUAA (NP2014403, NJ20140004) and a Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions.

文章分享

摘要/Abstract

以二氧化锗和二水合醋酸锌为原料,采用水热法制备了锗酸锌纳米棒,并将其与氧化石墨烯复合,制备了石墨烯包覆的锗酸锌纳米棒三维复合材料. SEM等测试表明,锗酸锌纳米棒均匀地穿插在石墨烯片中,阻止了石墨烯片之间相互堆垛,而石墨烯片层之间相互连接,形成三维的空间导电网络,提高了材料的电子导电性.电化学测试表明,石墨烯片作为稳定的框架,能够有效缓冲活性物质在脱嵌锂过程中产生的体积变化,在500 mA·g^-1电流密度下循环190次后, Zn₂GeO₄@RGO复合材料的嵌锂容量仍有1189.5 mAh·g^-1;在3.2 A·g^-1的大电流密度下,嵌锂容量达到449.5mAh·g^-1,表明该复合材料具有优异的长循环稳定性和良好的倍率性能.

关键词: 锂离子电池, 负极材料, 锗酸锌纳米棒, 还原氧化石墨烯, 水热法

Commercial graphite anode material for lithium-ion batteries (LIB) with a theoretical specific capacity of 372 mAh·g^-1 is unable to satisfy the requirements of increasing mobility and high energy demands. Therefore, it is necessary to develop alternative anode material with high specific capacity. In recent years, a large amount of research has been worked out in the area of high capacity anode materials, for example, silicon (Si) and germanium (Ge). However, the large volume changes of Si and Ge during the charge and discharge process result in the cracking and pulverization of active material and delamination from the current collector, leading to a rapid decay during the cycling. As a semiconductor, Zn₂GeO₄ possesses a high capacity of 1443 mAh·g^-1 which is 90.19% as high as Ge. Nevertheless, the weight rate of germanium element in Zn₂GeO₄ is only 27.15%, which can effectively cut down the cost of anode material. In this work, Zn₂GeO₄ nanorods were synthesized through a hydrothermal method by using GeO₂ and Zn(CH₃COO)2·2H₂O and combined with RGO to form a 3D composite. In a typical synthesis, 1.10 g Zn(CH₃COO)2·2H₂O and 0.52 g GeO₂ was added into 15 mL deionized (DI) water and the pH of the mixture was adjusted to 7~8 by using NaOH aqueous solution. Then, the hydrothermal treatment was performed at 140℃ for 24 h in an oven to obtain Zn₂GeO₄ nanorods. Finally, the Zn₂GeO₄ nanorods were filtrated with GO to form a uniform membrane and reduced by hydrazine hydrate. The Zn₂GeO₄ nanorods and Zn₂GeO₄@RGO composite were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), Raman spectroscopy, etc. SEM and TEM testified that Zn₂GeO₄ nanorods were firmly adhered on the surface of graphene sheets, which can effectively avoid the stacking of graphene sheets. The graphene sheets connected with each other to form an electric conductive network, which can improve the electrical conductivity of the composite. Furthermore, the electrodes are fabricated without conductive additive that can improve the weight ratio of the active material in the whole electrodes. The excellent electrochemical performance showed that the 3D architecture electrode which worked as a stable framework to accommodate the volume change of active material during Li+insertion/extraction. It delivers a specific capacity of 1189.5 mAh·g^-1 at 500 mA·g^-1 after 190 discharge/charge cycles. When at different current densities of 0.8, 1.6, 3.2 A·g^-1, the capacities were found to be about 880, 700, 450 mAh·g^-1, respectively. Even at a high current density of 6.4 A·g^-1, the capacity can maintain about 250 mAh·g^-1. These results indicate that the composite possesses outstanding cycling stability and excellent rate performance.

Key words: lithium-ion batteries, anode materials, zinc germanate nanorod, reduced graphene oxide, hydrothermal method

引用此文

童震坤, 方姗, 郑浩, 张校刚. 锗酸锌纳米棒@石墨烯复合负极材料的制备及储锂性质[J]. 化学学报, 2016, 74(2): 185-190.

Tong Zhenkun, Fang Shan, Zheng Hao, Zhang Xiaogang. Zn₂GeO₄ Nanorods@Graphene Composite as Anode Materials for Li-ion Batteries[J]. Acta Chim. Sinica, 2016, 74(2): 185-190.

导出引用 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

分享此文

参考文献

[1] Tarascon, J. M.; Armand, M. Nature 2001, 414, 359.
[2] Szczech, J. R.; Jin, S. Energy Environ. Sci. 2011, 4, 56.
[3] Hu, L. B.; Wu, H.; La Mantia, F.; Yang, Y. A.; Cui, Y. ACS Nano 2010, 4, 5843.
[4] Goodenough, J. B.; Kim, Y. Chem. Mater. 2010, 22, 587.
[5] Armand, M.; Tarascon, J. M. Nature 2008, 451, 652.
[6] Cheng, Y. W.; Lin, C. K.; Chu, Y. C.; Abouimrane, A.; Chen, Z. H.; Ren, Y.; Liu, C. P.; Tzeng, Y. H.; Auciello, O. Adv. Mater. 2014, 26, 3724.
[7] Fang, S.; Shen, L. F.; Tong, Z. K.; Zheng, H.; Zhang, F.; Zhang, X. G. Nanoscale 2015, 7, 7409.
[8] Fang, S.; Shen, L. F.; Zheng, H.; Zhang, X. G. J. Mater. Chem. A 2015, 3, 149.
[9] Zhao, T. P.; Gao, D. S.; Li, Z. H.; Lei, G. T.; Zhou, J. Acta Chim. Sinica 2009, 67, 1. (赵铁鹏, 高德淑, 李朝晖, 雷钢铁, 周姬, 化学学报, 2009, 67, 1.)
[10] Yoo, H.; Lee, J. I.; Kim, H.; Lee, J. P.; Cho, J.; Park, S. Nano Lett. 2011, 11, 4324.
[11] Chen, Y.; Yan, C.; Schmidt, O. G. Adv. Energy Mater. 2013, 3, 1269.
[12] Huang, G. Y.; Xu, S. M.; Wang, J. L.; Li, L. Y.; Wang, X. J. Acta Chim. Sinica 2013, 71, 1589. (黄国勇, 徐盛明, 王俊莲, 李林艳, 王学军, 化学学报, 2013, 71, 1589.)
[13] Graetz, J.; Ahn, C. C.; Yazami, R.; Fultz, B. J. Electrochem. Soc. 2004, 151, A698.
[14] Chan, C. K.; Zhang, X. F.; Cui, Y. Nano Lett. 2008, 8, 307.
[15] Cui, G. L.; Gu, L.; Zhi, L. J.; Kaskhedikar, N.; van Aken, P. A.; Mullen, K.; Maier, J. Adv. Mater. 2008, 20, 3079.
[16] Seng, K. H.; Park, M. H.; Guo, Z. P.; Liu, H. K.; Cho, J. Angew. Chem. Int. Ed. 2012, 51, 5657.
[17] Beaulieu, L. Y.; Eberman, K. W.; Turner, R. L.; Krause, L. J.; Dahn, J. R. Electrochem. Solid-State Lett. 2001, 4, A137.
[18] Key, B.; Bhattacharyya, R.; Morcrette, M.; Seznec, V.; Tarascon, J. M.; Grey, C. P. J. Am. Chem. Soc. 2009, 131, 9239.
[19] Liu, X. H.; Liu, Y.; Kushima, A.; Zhang, S. L.; Zhu, T.; Li, J.; Huang, J. Y. Adv. Energy Mater. 2012, 2, 722.
[20] Yi, R.; Feng, J.; Lv, D.; Gordin, M. L.; Chen, S.; Choi, D.; Wang, D. Nano Energy 2013, 2, 498.
[21] Feng, Y.; Li, X. D.; Shao, Z. P.; Wang, H. T. J. Mater. Chem. A 2015, 3, 15274.
[22] Chen, W. M.; Lu, L. Y.; Maloney, S.; Yang, Y.; Wang, W. Y. Phys. Chem. Chem. Phys. 2015, 17, 5109.
[23] Li, W. W.; Wang, X. F.; Liu, B.; Xu, J.; Liang, B.; Luo, T.; Luo, S. J.; Chen, D.; Shen, G. Z. Nanoscale 2013, 5, 10291.
[24] Geim, A. K. Angew. Chem. Int. Ed. 2011, 50, 6966.
[25] Wang, B.; Li, X. L.; Zhang, X. F.; Luo, B.; Jin, M. H.; Liang, M. H.; Dayeh, S. A.; Picraux, S. T.; Zhi, L. J. ACS Nano 2013, 7, 1437.
[26] Zou, F.; Hu, X. L.; Sun, Y. M.; Luo, W.; Xia, F. F.; Qie, L.; Jiang, Y.; Huang, Y. H. Chem. Eur. J. 2013, 19, 6027.
[27] Zou, F.; Hu, X. L.; Qie, L.; Jiang, Y.; Xiong, X. Q.; Qiao, Y.; Huang, Y. H. Nanoscale 2014, 6, 924.
[28] Li, W.; Yin, Y. X.; Xin, S.; Song, W. G.; Guo, Y. G. Energy Environ. Sci. 2012, 5, 8007.
[29] Rong, A.; Gao, X. P.; Li, G. R.; Yan, T. Y.; Zhu, H. Y.; Qu, J. Q.; Song, D. Y. J. Phys. Chem. B 2006, 110, 14754.
[30] Chen, Z.; Yan, Y.; Xin, S.; Li, W.; Qu, J.; Guo, Y. G.; Song, W. G. J. Mater. Chem. A 2013, 1, 11404.
[31] Ge, X.; Wang, X.; Wang, Z.; Yao, S.; Feng, J.; Liu, D. P.; Song, S. Y.; Zhang, H. J. Chem. Eur. J. 2015, 21, 14768.
[32] Li, W. W.; Wang, X. F.; Liu, B.; Luo, S. J.; Liu, Z.; Hou, X. J.; Xiang, Q. Y.; Chen, D.; Shen, G. Z. Chem. Eur. J. 2013, 19, 8650.
[33] Zhang, Y. L.; Hu, X. B.; Xu, Y. L.; Ding, M. L. Acta Chim. Sinica 2013, 71, 1341. (张永龙, 胡学步, 徐云兰, 丁明亮, 化学学报, 2013, 71, 1341.)
[34] Liu, X.; Xie, J. Y.; Zhao, H. L; Wang, K.; Tang, W. P.; Pan, Y. L.; Feng, Z. H.; Lv, P. P. Acta Chim. Sinica 2013, 71, 1011. (刘欣, 解晶莹, 赵海雷, 王可, 汤卫平, 潘延林, 丰震河, 吕鹏鹏, 化学学报, 2013, 71, 1011.)
[35] Sharma, Y.; Sharma, N.; Rao, G. V. S.; Chowdari, B. V. R. Adv. Funct. Mater. 2007, 17, 2855.
[36] Liu, J. P.; Li, Y. Y.; Ding, R. M.; Jiang, J.; Hu, Y. Y.; Ji, X. X.; Chi, Q. B.; Zhu, Z. H.; Huang, X. T. J. Phys. Chem. C 2009, 113, 5336.
[37] Wang, R.; Wu, S. P.; Lv, Y. C.; Lin, Z. Q. Langmuir 2014, 30, 8215.
[38] Wang, X. L.; Han, W. Q.; Chen, H. Y.; Bai, J. M.; Tyson, T. A.; Yu, X. Q.; Wang, X. J.; Yang, X. Q. J. Am. Chem. Soc. 2011, 133, 20692.
[39] Liu, J. P.; Li, Y. Y.; Huang, X. T.; Li, G. Y.; Li, Z. K. Adv. Funct. Mater. 2008, 18, 1448.
[40] Feng, J. K.; Xia, H.; Lai, M. O.; Lu, L. J. Phys. Chem. C 2009, 113, 20514.
[41] Park, M. H.; Cho, Y.; Kim, K.; Kim, J.; Liu, M. L.; Cho, J. Angew. Chem. Int. Ed. 2011, 50, 9647.
[42] Xue, X. Y.; Chen, Z. H.; Xing, L. L.; Yuan, S.; Chen, Y. J. Chem. Commun. 2011, 47, 5205.
[43] Seo, M. H.; Park, M.; Lee, K. T.; Kim, K.; Kim, J.; Cho, J. Energy Environ. Sci. 2011, 4, 425.

锗酸锌纳米棒@石墨烯复合负极材料的制备及储锂性质

Zn₂GeO₄ Nanorods@Graphene Composite as Anode Materials for Li-ion Batteries

PDF

可视化

被引次数

摘要/Abstract

引用此文

分享此文

参考文献

相关文章 15

编辑推荐

相关统计

本文评价

[1]	顾晓瑜, 李进, 孙千, 王朝阳. 微量量热法分析锂离子电池热失控过程[J]. 化学学报, 2024, 82(2): 146-151.
[2]	贾洋刚, 陈诗洁, 邵霞, 程婕, 林娜, 方道来, 冒爱琴, 李灿华. 高性能无钴化钙钛矿型高熵氧化物负极材料的制备及储锂性能研究[J]. 化学学报, 2023, 81(5): 486-495.
[3]	张雅岚, 苑志祥, 张浩, 张建军, 崔光磊. 高镍三元高比能固态锂离子电池的研究进展[J]. 化学学报, 2023, 81(12): 1724-1738.
[4]	常婉莹, 谭莹瑛, 吴静怡, 刘英杰, 蔡金海, 赖春艳. 三维结构Li_6.28La₃Zr₂Al_0.24O₁₂增强聚氧化乙烯基固态电解质的性能研究[J]. 化学学报, 2023, 81(12): 1708-1715.
[5]	刘稳, 王昱捷, 杨慧琴, 李成杰, 吴娜, 颜洋. 离子液体非共价诱导制备碳纳米管/石墨烯集流体用于钠金属负极[J]. 化学学报, 2023, 81(10): 1379-1386.
[6]	张爽, 杨成飞, 杨玉波, 冯宁宁, 杨刚. 基于废旧锂电池回收制备Li_xMO (x=0.79, 0.30, 0.08; M=Ni/Co/Mn)材料作为锂-氧气电池正极催化剂的电化学性能研究[J]. 化学学报, 2022, 80(9): 1269-1276.
[7]	毕文超, 张琳锋, 陈健, 田瑞雪, 黄昊, 姚曼. 单斜ZnP₂负极材料的锂化机理及性能[J]. 化学学报, 2022, 80(6): 756-764.
[8]	陈守潇, 刘君珂, 郑伟琛, 魏国祯, 周尧, 李君涛. 电/离子导体双包覆的LiNi_0.8Co_0.1Mn_0.1O₂锂离子电池阴极材料及其电化学性能[J]. 化学学报, 2022, 80(4): 485-493.
[9]	黄擎, 丁瑞, 陈来, 卢赟, 石奇, 张其雨, 聂启军, 苏岳锋, 吴锋. Na₂PO₃F对LiNi_0.83Co_0.11Mn_0.06O₂材料的复合改性及机理分析[J]. 化学学报, 2022, 80(2): 150-158.
[10]	邱凯, 严铭霞, 赵守旺, 安胜利, 王玮, 贾桂霄. Al掺杂的锂离子电池层状正极材料Li(Li_0.17Ni_0.17Al_0.04Fe_0.13Mn_0.49)O₂结构稳定性及氧离子氧化的理论研究[J]. 化学学报, 2021, 79(9): 1146-1153.
[11]	徐平, 张西华, 马恩, 饶富, 刘春伟, 姚沛帆, 孙峙, 王景伟. 退役锂离子电池碳/硫协同选择性提锂技术[J]. 化学学报, 2021, 79(8): 1073-1081.
[12]	李童心, 李东林, 张清波, 高建行, 孔祥泽, 樊小勇, 苟蕾. 大孔高镍LiNi_0.8Co_0.1Mn_0.1O₂正极材料的制备及其电化学性能研究[J]. 化学学报, 2021, 79(5): 678-684.
[13]	常智, 乔羽, 杨慧军, 邓瀚, 朱星宇, 何平, 周豪慎. 金属有机框架(MOFs)材料在锂离子电池及锂金属电池电解液中的应用[J]. 化学学报, 2021, 79(2): 139-145.
[14]	刘九鼎, 张宇栋, 刘俊祥, 李金翰, 邱晓光, 程方益. 磷酸锂原位包覆富锂锰基锂离子电池正极材料[J]. 化学学报, 2020, 78(12): 1426-1433.
[15]	任旭强, 李东林, 赵珍珍, 陈光琦, 赵坤, 孔祥泽, 李童心. 铝掺杂及钨酸锂表面包覆双效提升富锂锰基正极材料的循环稳定性[J]. 化学学报, 2020, 78(11): 1268-1274.

锗酸锌纳米棒@石墨烯复合负极材料的制备及储锂性质

Zn2GeO4 Nanorods@Graphene Composite as Anode Materials for Li-ion Batteries

PDF

可视化

被引次数

摘要/Abstract

引用此文

分享此文

参考文献

相关文章 15

编辑推荐

相关统计

本文评价

Zn₂GeO₄ Nanorods@Graphene Composite as Anode Materials for Li-ion Batteries