多孔钙钛矿型氧还原催化剂在柔性铝空气电池中的应用研究

doi:10.6023/A20030068

化学学报 ›› 2020, Vol. 78 ›› Issue (6): 557-564.DOI: 10.6023/A20030068 上一篇下一篇

研究论文

多孔钙钛矿型氧还原催化剂在柔性铝空气电池中的应用研究

税子怡^a, 何娜娜^a, 陈黎^a, 赵炜^a, 陈曦^a,b

a 西北大学化工学院西安 710069;
b 哥伦比亚大学地球与环境学院能源环境先进材料研究中心纽约 NY10027

投稿日期:2020-03-14 发布日期:2020-05-19
通讯作者: 赵炜, 陈曦 E-mail:zhaowei3313@nwu.edu.cn;xichen863@hotmail.com
基金资助:
项目受国家自然科学基金（No.11872302）、陕西省自然科学基础研究计划（No.2019JQ-431）和陕西省教育厅自然科学专项（No.20JK0927）资助.

Porous Perovskite towards Oxygen Reduction Reaction in Flexible Aluminum-Air Battery

Shui Ziyi^a, He Nana^a, Chen Li^a, Zhao Wei^a, Chen Xi^a,b

a Northwest University, School of Chemical Engineering, Xi'an 710069;
b Columbia University, Department of Earth and Environmental Engineering, New York NY 10027

Received:2020-03-14 Published:2020-05-19
Supported by:
Project supported by the National Natural Science Foundation of China (No. 11872302), the Natural Science Basic Research Program of Shaanxi Province (No. 2019JQ-431) and the Shaanxi Provincial Department of Education Natural Science Special Project (No. 20JK0927).

文章分享

摘要/Abstract

钙钛矿型催化材料作为贵金属的低成本替代物受到广泛关注，其用作氧还原反应催化剂具有非常可观活性和稳定性.目前相关工作主要集中在使用钙钛矿制备技术影响元素组成、形态、表面积和结构控制等方面.对于普遍存在的钙钛矿（ABO₃）材料而言，制备过程煅烧温度较高导致合成材料比表面积通常较小，限制了其在非均相催化反应中活性的提升.本文借助无机模板SiO₂制备具有高活性的大比表面的钙钛矿型催化材料La_0.7Sr_0.3MnO₃（LSMO）.测试结果表明，模板法LSMO具有非常可观的比表面积（31.1825 m²·g^-1），用在柔性铝空气电池中放电电压相比于无模板法和溶胶凝胶法可分别提高8.2%和24.5%，且在大电流放电下性能衰退明显减缓.在电池变形状态下，输出电压可稳定在1.38 V以上.不仅为燃料电池商业化提供了解决方案，同时为未来可变性电源发展提供了新方向.

关键词: 钙钛矿氧化物, 比表面积, 氧还原反应, 催化活性, 柔性铝空气电池

Perovskite-type catalytic materials have received wide attention as high-performance and low-cost alternatives to precious metal catalysts on the market at present, which have much considerable activity and stability as catalysts for oxygen reduction reactions. Current efforts are mainly focused on the use of perovskite make-up and preparation techniques to influence elemental composition, morphology, surface area, and structural control. For a typical perovskite oxide (ABO₃), due to the high calcination temperature in the preparation process, the perovskite material usually has a small specific surface area, which limits the increase of activity in heterogeneous catalytic reactions. In this paper, the perovskite La_0.7Sr_0.3MnO₃ (LSMO) material with large specific surface and high catalytic activity is prepared by means of the SiO₂ template. The physicochemical properties of the synthesized materials are characterized by scanning electron microscope (SEM), energy dispersed X-ray spectroscopy (EDS), X-ray diffraction (XRD) and BET. The catalytic activity of LSMO as an oxygen reduction reaction (ORR) catalyst is measured by a rotating disk test system. After that, the catalyst material is applied to a flexible aluminum-air battery and its discharge behavior and flexibility is studied and tested. The test results show that the LSMO prepared by template method has a large specific surface area (31.1825 m²·g^-1), and pore volume (0.161113 cm³·g^-1), and it also shows higher electrocatalytic activity in the electrochemical test system. When it is used in aluminum-air batteries, the activity of 3D porous LSMO is significantly better than that of sheet and bulk LSMO. The aluminum-air battery assembled by LSMO prepared by the template method has a higher discharge voltage (up to 1.46 V) at a constant current. Compared to the template-free method and the sol-gel method, the discharge voltage in flexible aluminum-air battery can be increased by 8.2% and 24.5%, respectively, and the performance degradation is significantly slowed during high-current discharge. The specific capacity and energy density of the battery are up to 1048.6 mA·h·g^-1 and 1020.6 mW·h·g^-1, respectively. When the battery is in a deformed state, its output voltage can be stabilized above 1.38 V. Once released, the voltage can be immediately restored to over 99% of the initial value. This paper not only provides a solution for the commercialization of fuel cell, but also provides a new direction for the future development of variable power supply.

Key words: perovskite oxide, specific surface area, oxygen reduction reaction, catalytic activity, flexible aluminum-air battery

引用此文

税子怡, 何娜娜, 陈黎, 赵炜, 陈曦. 多孔钙钛矿型氧还原催化剂在柔性铝空气电池中的应用研究[J]. 化学学报, 2020, 78(6): 557-564.

Shui Ziyi, He Nana, Chen Li, Zhao Wei, Chen Xi. Porous Perovskite towards Oxygen Reduction Reaction in Flexible Aluminum-Air Battery[J]. Acta Chimica Sinica, 2020, 78(6): 557-564.

导出引用 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

分享此文

参考文献

[1] Song, M. J.; Shin, M. W. Appl. Surf. Sci. 2014, 320, 435.
[2] Arora, P.; Zhang, Z. J. Chem. Rev. 2004, 104, 4419
[3] Xu, Y.; Zhao, Y.; Ren, J.; Zhang, Y.; Peng, H. Angew. Chem., Int. Ed. 2016, 55, 7979.
[4] Que, Y.; Qi, M.; Shi, P. Chin. Battery Ind. 2019, 23, 147. (阙奕鹏, 齐敏杰, 史鹏飞, 电池工业, 2019, 23, 147.)
[5] Xie, K.; Wei, B. Adv. Mater. 2014, 26, 3592.
[6] Cheng, F.; Chen, J. Chem. Soc. Rev. 2012, 41, 2172.
[7] Cheng, F.; Chen, J. Acta Chim. Sinica 2013, 71, 473. (程方益, 陈军, 化学学报, 2013, 71, 473.)
[8] Hong, Q.; Lu, H. Sci. Rep. 2017, 7, 3378.
[9] Li, Y. C.; Xu, Z. C.; Gasteiger, H. A.; Chen, S.; Hamad-Schifferli, K.; Yang, S.-H. J. Am. Chem. Soc. 2010, 132, 12170.
[10] Meng, H.; Shen, P. K. Electrochem. Commun. 2006, 8, 588.
[11] Hao, J.; Liu, Y.; Li, W.; Li, J. Mater. Rev. 2019, 33, 127. (郝佳瑜, 刘易斯, 李文章, 李洁, 材料导报, 2019, 33, 127.)
[12] Jin, Q.; Pei, L.; Hu, Y.; Du, J.; Han, X.; Cheng, F.; Chen, J. Acta Chim. Sinica 2014, 72, 920. (靳琪, 裴龙凯, 胡宇翔, 杜婧, 韩晓鹏, 程方益, 陈军, 化学学报, 2014, 72, 920.)
[13] Wang, D.; Chen, X.; Evans, D.-G.; Yang, W. Nanoscale 2013, 5, 5312.
[14] Wang, Y.; Wei, Z. J. Electrochem. 2018, 24, 427. (王尧, 魏子栋, 电化学, 2018, 24, 427.)
[15] Yin, W.; Shen, Y.; Zou, F.; Hu, X.; Chi, B.; Huang, Y. ACS Appl. Mater. Interfaces 2015, 7, 4947.
[16] Liu, M.; Zhang, R.; Chen, W. Chem. Rev. 2014, 114, 5117.
[17] Liu, L.; Yuan, Z.; Qiu, C.; Liu, J. Solid State Ionics 2013, 241, 25.
[18] Wang, Y.; Zhang, L.; Hu, T. Acta Chim. Sinica 2015, 73, 316. (王瀛, 张丽敏, 胡天军, 化学学报, 2015, 73, 316.)
[19] Miyazaki, K.; Kawakita, K.; Abe, T.; Fukutsuka, T.; Kojima, K.; Ogumi, Z. J. Mater. Chem. 2011, 21, 1913.
[20] Lin, S.; Xu, S.-F.; Wang, J.-D.; Xie, C.-S.; Yuan, A.-H.; Han, G.-F.; Zhang, L.; Zhang, L.-M.; Li, Y.; Yan, Z.-M. Acta Chim. Sinica 2005, 63, 385. (林生岭, 徐绍芬, 王俊德, 谢春生, 袁爱华, 韩光范, 张琳, 张黎明, 李燕, 严豸明, 化学学报, 2005, 63, 385.)
[21] Takeguchi, T.; Yamanaka, T.; Takahashi, H.; Watanabe, H.; Kuroki, T.; Nakanishi, H.; Orikasa, Y.; Uchimoto, Y.; Takano, H.; Ohguri, N.; Matsuda, M.; Murota, T.; Uosaki, K.; Ueda, W. J. Am. Chem. Soc. 2013, 135, 11125.
[22] Xue, Y.; Miao, H.; Sun, S.; Wang, Q.; Li, S.; Liu, Z. J. Power Sources 2017, 342, 192.
[23] Stoerzinger, K. A.; Lü, W.; Li, C.; Ariando; Venkatesan, T.; Yang, S.-H. J. Phys. Chem. Lett. 2015, 6, 1435.
[24] Hu, J.; Wang, L.; Shi, L.; Huang, H. J. Power Sources 2014, 269, 144.
[25] Liu, Y.; Dai, H.; Du, Y.; Deng, J.; Zhang, L.; Zhao, Z.; Au, C. T. J. Catal. 2012, 287, 149.
[26] Lee, Y. C.; Peng, P. Y.; Chang, W. S.; Huang, C. M. J. Taiwan Chem. Eng. 2014, 45, 2334.
[27] Stöber, W.; Fink, A.; Bohn, E. J. Colloid Interface Sci. 1968, 26, 62.
[28] Yang, C. H.; Chen, B. J.; Lu, J.; Yang, J. H.; Zhou, J.; Chen, Y. M.; Suo, Z. Extreme Mech. Lett. 2015, 25, 59.
[29] Tan, P.; Chen, B.; Xu, H.; Zhang, H.; Cai, W.; Ni, M.; Liu, M.; Shao, Z. Energy Environ. Sci. 2017, 10, 2056.
[30] Song, S.-D.; Tang, Z.-Y.; Pan, L.-Z.; Nan, J.-M. Acta Chim. Sinica 2005, 63, 363. (宋世栋, 唐致远, 潘丽珠, 南俊民, 化学学报, 2005, 63, 363.)
[31] Liu, Y.; Li, J.; Li, W.; Li, Y.; Zhan, F.; Tang, H.; Chen, Q. Int. J. Hydrogen Energy 2016, 41, 10354.
[32] Zhang, Z.; Zuo, C.; Liu, Z.; Yu, Y.; Zuo, Y.; Song, Y. J. Power Sources 2014, 251, 470.

多孔钙钛矿型氧还原催化剂在柔性铝空气电池中的应用研究

Porous Perovskite towards Oxygen Reduction Reaction in Flexible Aluminum-Air Battery

PDF

可视化

摘要/Abstract

引用此文

分享此文

参考文献

相关文章 15

编辑推荐

相关统计

本文评价

[1]	李萍, 杨琪玉, 曾婧, 张然, 陈秋燕, 闫飞. 氟掺杂对可逆固体氧化物电池性能的影响及相关动力学研究[J]. 化学学报, 2024, 82(1): 36-45.
[2]	陈其文, 张先正. 纳米酶介导的炎性肠道疾病治疗研究进展^★[J]. 化学学报, 2023, 81(8): 1043-1051.
[3]	闫绍兵, 焦龙, 何传新, 江海龙. ZIF-67/石墨烯复合物衍生的氮掺杂碳限域Co纳米颗粒用于高效电催化氧还原[J]. 化学学报, 2022, 80(8): 1084-1090.
[4]	王丹, 封波, 张晓昕, 刘亚楠, 裴燕, 乔明华, 宗保宁. 基于热解ZIF-8的氮掺杂碳电化学氧还原合成过氧化氢催化剂[J]. 化学学报, 2022, 80(6): 772-780.
[5]	耿元昊, 林小秋, 孙亚昕, 李惠雨, 秦悦, 李从举. 双金属导电金属有机框架材料Ni/Co-CAT的制备及其氧还原催化性能研究[J]. 化学学报, 2022, 80(6): 748-755.
[6]	鲁效庆, 曹守福, 魏晓飞, 李邵仁, 魏淑贤. S掺杂Fe-NC单原子催化剂氧还原机理研究[J]. 化学学报, 2020, 78(9): 1001-1006.
[7]	李威, 冉铁成, 张瑜, 何威, 马继飞, 汪启胜, 张继超, 诸颖. SiO₂介导的5 nm金颗粒的高效富集及其催化活性研究[J]. 化学学报, 2020, 78(2): 170-176.
[8]	楚婉怡, 唐笑, 李振, 林景诚, 钱觉时. 液相合成超薄TiO₂纳米片微结构影响因素研究[J]. 化学学报, 2018, 76(7): 549-555.
[9]	陈鑫, 鄢慧君, 夏定国. 锗纳米管催化的氧还原反应:催化性能和机理研究[J]. 化学学报, 2017, 75(2): 189-192.
[10]	万刚, 付宇昂, 郭佳宁, 向中华. 光电多孔共价有机材料的研究进展[J]. 化学学报, 2015, 73(6): 557-578.
[11]	赵洋, 王笑颜, 张崇, 蒋加兴. 四苯基乙烯基共轭微孔聚合物的制备及其气体吸附[J]. 化学学报, 2015, 73(6): 634-640.
[12]	王瀛, 张丽敏, 胡天军. 金属空气电池阴极氧还原催化剂研究进展[J]. 化学学报, 2015, 73(4): 316-325.
[13]	韩若冰, 芦姗, 王艳杰, 张雪华, 吴强, 贺涛. SO₄^-和I^-共掺杂的聚苯胺对电极在染料敏化太阳电池中的应用[J]. 化学学报, 2015, 73(10): 1061-1068.
[14]	张婷婷, 王海涛, 马和平, 孙福兴, 崔小强, 朱广山. 以芘-炔为基块的共价有机骨架材料的设计合成与表征[J]. 化学学报, 2013, 71(12): 1598-1602.
[15]	张栋, 张存中, 穆道斌, 吴伯荣, 吴锋. 氧还原反应中的银基催化剂[J]. 化学学报, 2013, 71(08): 1101-1110.