Morphology and Mechanical Properties of Chitosan/ Graphene Oxide Nanocomposites

Zhao Qian1,Qiu Dongfang2,Wang Xiaoyan3,Liu Tianxi*,3   

  1. (1 Journal Editorial Department of Nanyang Normal University,, Nanyang 447733006611) (2 Chemistry and Pharmaceutical Engineering College,, Nanyang Normal University,, Nanyang 447733006611) (3 Key Laboratory of Molecular Engineering of Polymers of Ministry of Education,, Department of Macromolecular Science,, Fudan University,, Shanghai 220000443333)
  • Received:2010-12-31 Revised:2011-01-25 Published:2011-01-30
  • Contact: Tianxi Liu E-mail:txliu@fudan.edu.cn

Chitosan/graphene oxide nanocomposites were prepared by solution blending method. TEM observations showed that the graphene oxide (GO) was well dispersed in chitosan matrix. By incorporating GO into chitosan, both tensile strength and modulus of the nanocomposites were significantly increased due to the fine dispersion of GO and strong interfacial interactions between GO and the chitosan matrix, while their elongation at break decreased to certain extent.

Key words: graphene, chitosan, nanocomposites