LiPF₆/三氟乙酰胺室温熔盐的制备及在碳-碳电容器中的性能

左晓希^a, 李奇^a, 刘建生^b, 肖信^a, 范成杰^a, 南俊民^a

a 华南师范大学化学与环境学院广州 510006;
b 广州天赐高新材料股份有限公司广州 510760

投稿日期:2011-10-21 修回日期:2011-11-29 发布日期:2011-11-30
通讯作者: 南俊民
基金资助:
国家自然科学基金青年基金(No. 21003045)、广东省产学研计划(No. 2009B090300389)及2011 广州市黄埔区科技计划资助项目.

Preparation and Performances of Room Molten Salt as Electrolyte in Carbon-carbon Capacitor Based on LiPF₆ and Trifluoroacetamide

Zuo Xiaoxi^a, Li Qi^a, Liu Jiansheng^b, Xiao Xin^a, Fan Chengjie^a, Nan Junmin^a

a School of Chemistry and Environment, South China Normal University, Guangzhou 510006;
b Guangzhou Tinci Materials Technology Co., Ltd., Guangzhou 510760

Received:2011-10-21 Revised:2011-11-29 Published:2011-11-30
Supported by:
Project was supported by the Young Scientists Fund of the National Natural Science Foundation of China (No. 21003045), the Department of Guangdong Province produced in academic and research projects (No. 2009B090300389) and Huangpu District, Guangzhou Science and Technology Project, 2011.

文章分享

摘要/Abstract

利用LiPF₆ 和三氟乙酰胺为前驱物, 制备了低共熔温度约为-62 ℃的室温熔盐, 并测试了该熔盐作为碳-碳电化学电容器(EDLCs)电解液时的性能. 其中, 使用差示扫描量热法(DSC)和红外光谱法(FTIR)分析了不同LiPF₆ 和三氟乙酰胺配比熔盐的热稳定性, 拟制了该二元组分的共熔相图, 认为LiPF₆ 和三氟乙酰胺极性基团间的氢键作用促成了室温熔盐的形成. 循环伏安(CV)、交流阻抗(EIS)和电导等测定结果表明, 所制备的LiPF₆/三氟乙酰胺电解液的室温电导率为1.30 mS/cm, 电化学窗口大于5.6 V, 大于60 ℃的使用温度, 作为电解液可满足碳-碳EDLCs 的使用要求.

关键词: 室温熔盐, LiPF₆, 三氟乙酰胺, 热性能, 电化学性能

A novel room molten salt with an eutectic temperature of about -62 ℃ is prepared using LiPF₆ and trifluoroacetamide as precursors. And then its performances are evaluated in carbon-carbon electrochemical double layer capacitor (EDLC) as electrolyte. The thermal properties of the complex electrolyte with different molar ratios are characterized and then the liquid-solid phase diagram is presented by using differential scanning calorimeter (DSC) and Fourier transform infrared spectroscopy (FTIR). The hydrogen bonding interaction between LiPF₆ and trifluoroacetamide molecules is attributed to the formation of the as-prepared molten salt. In addition, the results of cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and conductance tests show that the as-prepared LiPF₆/trifluoroacetamide electrolyte has a maximum conductance at room temperature, i.e. 1.30 mS/cm, a stable electrochemical window of ca. 5.6 V, an applicable temperature of more than 60 ℃, suggesting it is a promising electrolyte candidate for carbon-carbon EDLCs.

Key words: room molten salt, LiPF₆, trifluoroacetamide, thermal property, electrochemical performance

引用此文

左晓希, 李奇, 刘建生, 肖信, 范成杰, 南俊民. LiPF₆/三氟乙酰胺室温熔盐的制备及在碳-碳电容器中的性能[J]. 化学学报, 2012, 70(04): 367-371.

Zuo Xiaoxi, Li Qi, Liu Jiansheng, Xiao Xin, Fan Chengjie, Nan Junmin. Preparation and Performances of Room Molten Salt as Electrolyte in Carbon-carbon Capacitor Based on LiPF₆ and Trifluoroacetamide[J]. Acta Chimica Sinica, 2012, 70(04): 367-371.

导出引用 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

分享此文

参考文献

1 Chang, J. K.; Lee, M. T.; Cheng, C. W.; Tsai, W. T.; Deng, M. J.; Sun, I. W. Electrochem. Solid-State Lett. 2009, 12, A19.

2 McManis, G.; Fletcher, A.; Bliss, D.; Miles, M. J. Electroanal. Chem. 1985, 190, 171.

3 Caldeira, M. O. S. P.; Sequeira, C. A. C. Molten Salt Forum 1993, 1, 407

4 Yu, Z.; Li, H.; Li, K.; Qin, D.; Deng, M.; Li, D. Electrochim. Acta 2010, 55, 895.

5 Xu, B.; Wu, F.; Chen, R.; Cao, G.; Chen, S.; Yang, Y. J. Power Sources 2010, 195, 2118.

6 Liang, H.; Li, H.; Wang, Z.; Wu, F.; Chen, L.; Huang, X. J. Phys. Chem. B 2001, 105, 9966.

7 Li, Z.; Liu, L.; Cao, Q.; Wang, J.; Yan, T. Acta Phys. Chim. Sin. 2007, 23, 983 (in Chinese). (李姝, 刘磊, 曹臻, 汪继强, 言天英, 物理化学学报, 2007, 23, 983.)

8 Chen, R.; Wu, F.; Liang, H.; Mao, L. Acta Phys. Chim. Sin. 2004, 20, 323 (in Chinese). (陈人杰, 吴锋, 粱宏莹, 毛立彩, 物理化学学报, 2004, 20, 323.)

9 Chen, R.; Wu, F. Acta Phys. Chim. Sin. 2005, 21, 177 (in Chinese). (陈人杰, 吴锋, 物理化学学报, 2005, 21, 177.)

10 Xie, B.; Li, L.; Li, H.; Chen, L. Solid State Ionics 2009, 180, 688.

11 Chang, J. K.; Lee, M. T.; Cheng, C. W.; Tsai, W. T.; Deng, M. J.; Hsieh, Y. C.; Sun, I. W. J. Mater. Chem. 2009, 19, 3732.

12 Wu, F.; Chen, R.; Li, L.; Xu, B.; Chen, S.; Wang, G. J. Power Sources 2008, 184, 402.

13 Huang, J.; Sumpter, B. G.; Meunier V. Angew. Chem., Int. Ed. 2008, 47, 520.

14 Chen, R.; Wu, F.; Xu, B.; Li, L.; Qiu, X.; Chen, S. J. Electrochem. Soc. 2007, 154, A703.

15 Chen, R.; Wu, F.; Li, L.; Xu, B.; Qiu, X.; Chen, S. J. Phys. Chem. C 2007, 111, 5184.

16 Chen, R.; Wu, F.; Li, L.; Qiu, X.; Chen, L.; Chen, S. Vib. Spectrosc. 2007, 44, 297.

17 Song, S. W.; Richardson, T. J.; Zhuang, G. V.; Devine, T. M.; Evans, J. W. Electrochim. Acta 2004, 49, 1483.

18 Chen, R.; Wu, F.; Liang, H.; Li, L.; Xu, B. J. Electrochem. Soc. 2005, 152, A1979.

19 Li, Q.; Zuo, X.; Liu, J.; Xiao, X.; Shu, D.; Nan, J. Electrochim. Acta 2011, 58, 330.

20 De Levies, R. Electrochim. Acta 1963, 8, 751.

21 Okajima, K.; Ohta, K.; Sudoh, M. Electrochim. Acta 2005, 50, 2227.

[1]	李萍, 杨琪玉, 曾婧, 张然, 陈秋燕, 闫飞. 氟掺杂对可逆固体氧化物电池性能的影响及相关动力学研究[J]. 化学学报, 2024, 82(1): 36-45.
[2]	刘士琨, 邓程维, 姬峰, 闵宇霖, 李和兴. 高温质子交换膜燃料电池中阴极双催化层孔结构的设计研究^★[J]. 化学学报, 2023, 81(9): 1135-1141.
[3]	李燕丽, 于丹丹, 林森, 孙东飞, 雷自强. α-MnO₂纳米棒/多孔碳正极材料的制备及水系锌离子电池性能研究[J]. 化学学报, 2021, 79(2): 200-207.
[4]	梁其梅, 郭昱娇, 郭俊明, 向明武, 刘晓芳, 白玮, 宁平. 亚微米去顶角八面体LiNi_0.08Mn_1.92O₄正极材料制备及高温电化学性能[J]. 化学学报, 2021, 79(12): 1526-1533.
[5]	李金华, 卓庆德, 卓凯玥, 陈大发, 夏海平. 铱杂碳龙配合物的合成及反应性[J]. 化学学报, 2021, 79(1): 71-80.
[6]	渠璐平, 任彤, 王宁, 史月丽, 庄全超. 硬碳材料电极首周嵌钠过程的电化学阻抗谱研究[J]. 化学学报, 2019, 77(7): 634-640.
[7]	宋学霞, 李继成, 李朝晖, 李喜飞, 丁燕怀, 肖启振, 雷钢铁. 钾掺杂对钒酸钠纳米片储钠性能的影响[J]. 化学学报, 2019, 77(7): 625-633.
[8]	常世磊, 梁风, 姚耀春, 马文会, 杨斌, 戴永年. 金属二氧化碳电池的研究进展[J]. 化学学报, 2018, 76(7): 515-525.
[9]	郑媛, 罗静, 魏玮, 刘晓亚. Pickering乳液法制备聚苯胺-石墨烯空心微球[J]. 化学学报, 2017, 75(4): 391-397.
[10]	杨春, 龚正良, 赵文高, 杨勇. 富锂正极材料xLi₃NbO₄·(1-x)LiMO₂(M=Mn,Co;0 < x < 1)的制备及电化学性能研究[J]. 化学学报, 2017, 75(2): 212-217.
[11]	刘清朝, 马诗喻, 徐吉静, 李中军, 张新波. 锂-空气二次电池关键材料与器件的设计与制备[J]. 化学学报, 2017, 75(2): 137-146.
[12]	孔丽娟, 周晓燕, 范赛英, 李在均, 顾志国. 组氨酸功能化石墨烯量子点@纳米硅负极材料的制备及电化学性能研究[J]. 化学学报, 2016, 74(7): 620-628.
[13]	刘欣, 解晶莹, 赵海雷, 王可, 汤卫平, 潘延林, 丰震河, 吕鹏鹏. 锂离子电池Sn₃₀Co₃₀C₄₀三元合金负极材料的制备与性能研究[J]. 化学学报, 2013, 71(07): 1011-1016.
[14]	马利, 梁卫朝, 甘孟瑜, 黄超群, 谷静连, 杨雅文, 李王林, 张峰. APS/NaClO 复合氧化剂对乳液法合成聚苯胺的微观形貌及其电化学性能的影响[J]. 化学学报, 2012, 70(10): 1207-1212.
[15]	马利, 谷静连, 甘孟瑜, 梁卫朝, 黄超群, 杨雅文, 张峰, 李王林. 砂磨法制备聚苯胺及其电化学性能的研究[J]. 化学学报, 2011, 69(24): 3007-3012.

LiPF₆/三氟乙酰胺室温熔盐的制备及在碳-碳电容器中的性能

Preparation and Performances of Room Molten Salt as Electrolyte in Carbon-carbon Capacitor Based on LiPF₆ and Trifluoroacetamide

PDF

可视化

摘要/Abstract

引用此文

分享此文

参考文献

相关文章 15

编辑推荐

相关统计

本文评价