热解聚苯胺/碳纳米笼复合物制备氮掺杂碳材料及其氧还原性能研究

doi:10.6023/A15050354

化学学报 ›› 2015, Vol. 73 ›› Issue (8): 793-798.DOI: 10.6023/A15050354 上一篇下一篇

研究通讯

热解聚苯胺/碳纳米笼复合物制备氮掺杂碳材料及其氧还原性能研究

许智慧, 沈丽明, 吴强, 孙涛, 徐宇洋, 黎聃勤, 杜玲玉, 杨立军, 王喜章, 胡征

介观化学教育部重点实验室南京大学化学化工学院南京 210093

投稿日期:2015-05-24 发布日期:2015-07-07
通讯作者: 吴强 E-mail:wqchem@nju.edu.cn
基金资助:
项目受国家自然科学基金(Nos. 51232003, 21173115, 21203092, 21473089)和“973”项目(No. 2013CB932902)资助.

Oxygen Reduction Performance of the Nitrogen-Doped Carbon Materials Pyrolyzed from Polyaniline/Carbon Nanocage Composites

Xu Zhihui, Shen Liming, Wu Qiang, Sun Tao, Xu Yuyang, Li Danqin, Du Lingyu, Yang Lijun, Wang Xizhang, Hu Zheng

Key Laboratory of Mesoscopic Chemistry of MOE, School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210093

Received:2015-05-24 Published:2015-07-07
Supported by:
Project supported by the National Natural Science Foundation of China (Nos. 51232003, 21173115, 21203092, 21473089) and “973” program (No. 2013CB932902).

文章分享

摘要/Abstract

将含氮聚合物聚苯胺(PANI)均匀地担载到具有大比表面积、多级孔结构和高导电性的3D碳纳米笼(CNC)表面, 再热解PANI制得了N掺杂位富集于表面、且具有优良导电性的碳基纳米材料. 通过改变热解温度和前驱物中PANI的含量, 对热解产物的表面N含量和导电性进行了调控. 优化得到的NCNC-2-900催化剂具有优异的氧还原反应(ORR)催化性能, 其起始电位高(-46 mV vs Ag/AgCl), 明显优于体相N掺杂的CNC (-105 mV), 且稳定性好(运行10 h后仍保留96%活性). 该结果表明在保持良好导电性的同时增加表面N掺杂位是提高碳基材料ORR活性的有效途径.

关键词: 氮掺杂, 聚苯胺热解, 碳纳米笼, 氧还原, 燃料电池

Fuel cells can efficiently convert chemical energy of fuels into electrical energy in a green manner, representing one of the most promising movable power sources. The main bottleneck for the wide application of fuel cells is the sluggish oxygen reduction reaction (ORR) which is usually catalyzed by expensive and unstable Pt catalysts. Hence, the exploration of cost-efficient and long-life ORR electrocatalysts is of great significance. Recently carbon-based metal-free ORR electrocatalysts have attracted much interest due to their superior activity and stability as well as the abundance and low cost. It is generally accepted that nitrogen doping of carbon materials boost the ORR activity by breaking the electroneutrality of carbon layer and activating π electrons. Considering that the embedded N doping sites are useless for ORR but significantly affect electron conduction, the carbon materials with N-enriched surface of high activity and pristine carbon bulk of high conductivity should present better ORR performance than the bulk N-doped counterpart. In this contribution, we report an efficient strategy for the synthesis of ORR electrocatalysts with surface enriched N doping and high conductive bulk by dispersing polyaniline (PANI) on the surface of 3D hierarchical carbon nanocages (CNC), followed by heat treatment in Ar. The N content and conductivity of the pyrolyzed products are regulated by changing the pyrolysis temperature and the weight ratio of PANI/CNC composite. The optimized electrocatalyst with the N content of 2.21 at% and the conductivity of 203 S·m^-1 exhibits excellent ORR catalytic performance with high onset potential of -46 mV vs Ag/AgCl, obvious superior to the bulk N-doped CNC (-105 mV). This catalyst also possesses high stability (96% activity retention after 10 h continuous tests) and dominated 2-electron pathway for ORR with transferred electron number of 2.8. This result suggests an efficient route to improve the ORR activity of carbon-based materials by increasing the N content enriched at the surface while keeping their high conductivity.

Key words: nitrogen doping, polyaniline pyrolysis, carbon nanocages, oxygen reduction, fuel cells

引用此文

许智慧, 沈丽明, 吴强, 孙涛, 徐宇洋, 黎聃勤, 杜玲玉, 杨立军, 王喜章, 胡征. 热解聚苯胺/碳纳米笼复合物制备氮掺杂碳材料及其氧还原性能研究[J]. 化学学报, 2015, 73(8): 793-798.

Xu Zhihui, Shen Liming, Wu Qiang, Sun Tao, Xu Yuyang, Li Danqin, Du Lingyu, Yang Lijun, Wang Xizhang, Hu Zheng. Oxygen Reduction Performance of the Nitrogen-Doped Carbon Materials Pyrolyzed from Polyaniline/Carbon Nanocage Composites[J]. Acta Chim. Sinica, 2015, 73(8): 793-798.

导出引用 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

分享此文

参考文献

[1] Chu, S.; Majumdar, A. Nature 2012, 488, 294.
[2] Wang, Z. H.; Shi, G. Y.; Xia, J. F.; Zhang, F. F.; Xia, Y. Z.; Li, Y. H.; Xia, L. H. Acta Chim. Sinica 2013, 71, 1225. (王宗花, 史国玉, 夏建飞, 张菲菲, 夏延致, 李延辉, 夏临华, 化学学报, 2013, 71, 1225.)
[3] Gasteiger, H. A.; Markovic, N. M. Science 2009, 324, 48.
[4] Gong, K. P.; Du, F.; Xia, Z. H.; Durstock, M.; Dai, L. M. Science 2009, 323, 760.
[5] Jiang, S. J.; Ma, Y. W.; Jian, G. Q.; Tao, H. S.; Wang, X. Z.; Fan, Y. N.; Lu, Y. N.; Hu, Z.; Chen, Y. Adv. Mater. 2009, 21, 4953.
[6] Wu, J. B.; Yang, H. Acc. Chem. Res. 2013, 46, 1848.
[7] Zhang, S.; Zhang, S.; Jiang, S. M.; Zhu, H. Y.; Guo, S. J.; Su, D.; Lu, G.; Sun, S. H. J. Am. Chem. Soc. 2014, 136, 7734.
[8] Chen, Z. W.; Higgins, D.; Yu, A. P.; Zhang, L.; Zhang, J. J. Energy Environ. Sci. 2011, 4, 3167.
[9] Liang, Y. Y.; Li, Y. G.; Wang, H. L.; Dai, H. J. J. Am. Chem. Soc. 2013, 135, 2013.
[10] Sun, T.; Wu, Q.; Che, R. C.; Bu, Y. F.; Jiang, Y. F.; Li, Y.; Yang, L. J.; Wang, X. Z.; Hu, Z. ACS Catal. 2015, 5, 1857.
[11] Qu, L.-T.; Liu, Y.; Baek, J. B.; Dai, L.-M. ACS Nano 2010, 4, 1321.
[12] Liu, R.-L.; Wu, D.-P.; Feng, X.-L.; Müllen, K. Angew. Chem., Int. Ed. 2010, 49, 1.
[13] Chen, S.; Bi, J. Y.; Zhao, Y.; Yang, L. J.; Zhang, C.; Ma, Y. W.; Wu, Q.; Wang, X. Z.; Hu, Z. Adv. Mater. 2012, 24, 5593.
[14] Yang, L. J.; Jiang, S. J.; Zhao, Y.; Zhu, L.; Chen, S.; Wang, X. Z.; Wu, Q.; Ma, J.; Ma, Y. W.; Hu, Z. Angew. Chem., Int. Ed. 2011, 50, 7132.
[15] Zhao, Y.; Yang, L. J.; Chen, S.; Wang, X. Z.; Ma, Y. W.; Wu, Q.; Jiang, Y. F.; Qian, W. J.; Hu, Z. J. Am. Chem. Soc. 2013, 135, 1201.
[16] Liang, J.; Jiao, Y.; Jaroniec, M.; Qiao, S.-Z. Angew. Chem., Int. Ed. 2012, 51, 11496.
[17] Yang, Z.; Yao, Z.; Li, G.-F.; Fang, G.-Y.; Nie, H.-G.; Liu, Z.; Zhou, X.-M.; Chen, X.; Huang, S.-M. ACS Nano 2012, 6, 205.
[18] Liu, Z. W.; Peng, F.; Wang, H. J.; Yu, H.; Zheng, W. X.; Yang, J. Angew. Chem., Int. Ed. 2011, 50, 3257.
[19] Wang, L. W.; Feng, R.; Xia, J. Z.; Chen, S.; Wu, Q.; Yang, L. J.; Wang, X. Z.; Hu, Z. Acta Chim. Sinica 2014, 72, 1070. (王立伟, 冯瑞, 夏婧竹, 陈盛, 吴强, 杨立军, 王喜章, 胡征, 化学学报, 2014, 72, 1070.)
[20] Dai, L. M.; Xue, Y. H.; Qu, L. T.; Choi, H. J.; Baek, J. B. Chem. Rev. 2015, 115, 4823.
[21] Tian, G. L.; Zhang, Q.; Zhang, B. S.; Jin, Y. G.; Huang, J. Q.; Su, D. S.; Wei, F. Adv. Funct. Mater. 2014, 24, 5956.
[22] Wang, X. Q.; Lee, J. S.; Zhu, Q.; Liu, J.; Wang, Y.; Dai, S. Chem. Mater. 2010, 22, 2178.
[23] Chen, L.; Du, R.; Zhu, J. H.; Mao, Y. Y.; Xue, C.; Zhang, N.; Hou, Y. L.; Zhang, J.; Yi, T. Small 2015, 11, 1423.
[24] Yazdi, A. Z.; Fei, H. L.; Ye, R. Q.; Wang, G.; Tour, J.; Sundararaj, U. ACS Appl. Mater. Interfaces 2015, 7, 7786.
[25] Zhang, L. J.; Su, Z. X.; Jiang, F. L.; Yang, L. L.; Qian, J. J.; Zhou, Y. F.; Li, W. M.; Hong, M. C. Nanoscale 2014, 6, 6590.
[26] Xie, K.; Qin, X. T.; Wang, X. Z.; Wang, Y. N.; Tao, H. S.; Wu, Q.; Yang, L. J.; Hu, Z. Adv. Mater. 2012, 24, 347.
[27] Lyu, Z. Y.; Xu, D.; Yang, L. J.; Che, R. C.; Feng, R.; Zhao, J.; Li, Y.; Wu, Q.; Wang, X. Z.; Hu, Z. Nano Energy 2015, 12, 657.
[28] Liang, Y.-Y.; Wang, H.-L.; Zhou, J.-G.; Li, Y.-G.; Wang, J.; Regier, T.; Dai, H.-J. J. Am. Chem. Soc. 2012, 134, 3517.

热解聚苯胺/碳纳米笼复合物制备氮掺杂碳材料及其氧还原性能研究

Oxygen Reduction Performance of the Nitrogen-Doped Carbon Materials Pyrolyzed from Polyaniline/Carbon Nanocage Composites

PDF

可视化

被引次数

摘要/Abstract

引用此文

分享此文

参考文献

相关文章 15

编辑推荐

相关统计

本文评价

[1]	李萍, 杨琪玉, 曾婧, 张然, 陈秋燕, 闫飞. 氟掺杂对可逆固体氧化物电池性能的影响及相关动力学研究[J]. 化学学报, 2024, 82(1): 36-45.
[2]	刘士琨, 邓程维, 姬峰, 闵宇霖, 李和兴. 高温质子交换膜燃料电池中阴极双催化层孔结构的设计研究^★[J]. 化学学报, 2023, 81(9): 1135-1141.
[3]	刘佳, 陈光海, 陈轶群, 江杰涛, 肖霄, 吴强, 杨立军, 王喜章, 胡征. 碳热还原活化扩孔提升介观结构碳纳米笼超级电容器性能^★[J]. 化学学报, 2023, 81(7): 709-716.
[4]	刘金晶, 杨娜, 李莉, 魏子栋. 铂活性位空间结构调控氧还原机理的理论研究^★[J]. 化学学报, 2023, 81(11): 1478-1485.
[5]	王庆鑫, 崔勇, 李蕴琪, 卢善富, 相艳. Fe-N-C阴极催化层离聚物可控热解对膜电极性能与稳定性的影响研究^★[J]. 化学学报, 2023, 81(10): 1350-1356.
[6]	刘春梅, 高燕均, 陈鹏亮. 直接甲酸钠/铁氰化钾微流体燃料电池性能研究[J]. 化学学报, 2022, 80(9): 1256-1263.
[7]	王怡戈, 李航越, 吕泽伟, 韩敏芳, 孙凯华. 工业尺寸固体氧化物燃料电池高效及阳极安全运行条件研究[J]. 化学学报, 2022, 80(8): 1091-1099.
[8]	闫绍兵, 焦龙, 何传新, 江海龙. ZIF-67/石墨烯复合物衍生的氮掺杂碳限域Co纳米颗粒用于高效电催化氧还原[J]. 化学学报, 2022, 80(8): 1084-1090.
[9]	齐志豪, 高福杰, 周常楷, 曾誉, 吴强, 杨立军, 王喜章, 胡征. 氮掺杂碳纳米笼固载钌纳米粒子的费托合成性能[J]. 化学学报, 2022, 80(8): 1100-1105.
[10]	何家伟, 焦柳, 程雪怡, 陈光海, 吴强, 王喜章, 杨立军, 胡征. 金属有机框架衍生的空心碳纳米笼的结构调控与锂硫电池性能研究[J]. 化学学报, 2022, 80(7): 896-902.
[11]	王丹, 封波, 张晓昕, 刘亚楠, 裴燕, 乔明华, 宗保宁. 基于热解ZIF-8的氮掺杂碳电化学氧还原合成过氧化氢催化剂[J]. 化学学报, 2022, 80(6): 772-780.
[12]	耿元昊, 林小秋, 孙亚昕, 李惠雨, 秦悦, 李从举. 双金属导电金属有机框架材料Ni/Co-CAT的制备及其氧还原催化性能研究[J]. 化学学报, 2022, 80(6): 748-755.
[13]	于潇涵, 黄伟, 李彦光. 二维共价有机框架材料的可控合成及其光催化应用研究进展[J]. 化学学报, 2022, 80(11): 1494-1506.
[14]	高润洲, 李国昌, 陈轶群, 曾誉, 赵杰, 吴强, 杨立军, 王喜章, 胡征. 基于原位聚合凝胶电解质的碳纳米笼//三氧化钨纳米棒超级电容器[J]. 化学学报, 2021, 79(6): 755-762.
[15]	吕泽伟, 韩敏芳, 孙再洪, 孙凯华. 固体氧化物燃料电池运行初期电化学性能演变机制[J]. 化学学报, 2021, 79(6): 763-770.